Abstract:The practical application of MnFeOx catalyst is limited due to its narrow temperature window and poor resistance to alkali metal poisoning, such as K and Na. Alkali metal poisoning has always been a major factor in the deactivation of fixed-source denitration (deNOx) catalysts. Despite high activity at around 200(degrees)C , the catalyst's susceptibility to alkali metal poisoning hinders its effectiveness. In this study, a novel MnFeOx/H-Beta composite catalyst was prepared by the simple wet impregnation method. Beta zeolite, known for its large specific surface area compared to MnFeOx, special twelve-membered ring channel, and abundant acid sites, was introduced to adjust the acid and redox active sites. This resulted in MnFeOx/H-Beta having a wider temperature window and excellent resistance to K poisoning. Notably, the NOx conversion rate exceeded 80% between 180 and 460 C . K poisoning significantly reduces the acidity of the catalyst, as confirmed by various characterizations such as NH3TPD and NH3 adsorption in situ DRIFTs. After K poisoning, the total acid content of MnFeOx/H-Beta decreased from 14.99 to 9.47 mmol g(-1). The low acid content of MnFeOx allows the active sites to be easily covered by K, resulting in a reduction of the SCR performance, which can be attributed to the reduction of active nitrate species. The abundant acid sites of MnFeOx/H-Beta act as sacrificial sites and can coordinate with alkali metal K, thereby alleviating the poisoning of the catalyst to some extent. DFT calculations confirmed K binding to Bronsted acid sites on H-Beta zeolite, mitigating the detrimental impact of K on catalyst activity and lifetime. This research offers a pathway for designing efficient and alkali metal-resistant deNO(x )catalysts for real-world industrial applications.

Denitration catalyst containing tungsten tin manganese cerium composite oxide as well as preparation and application of denitration catalyst

Co-precipitation preparation method of composite oxide denitration catalyst

Denitration catalyst with tungstovanadophosphoric heteropolyacid as precursor and preparation method of denitration catalyst

Mixed synergistically-enhanced low-temperature SCR denitration catalyst and preparation method thereof

Low temperature denitration and synergetic desulfurization active carbon catalyst and preparation method thereof

Ordered mesoporous carbon loading Cu-Mn bi-metal denitration catalyst and preparation method thereof

SCR (selective catalytic reduction) denitration catalyst for accelerating ammonium hydrogen sulfate decomposition by low-temperature flue gas, preparation method and application

Ternary MnCoVO catalysts with remarkable deNO performance: Dual acid-redox sites control strategy

Discovering the Remarkable Denox Activity and Anti-K Poisoning of MnFeOx/H-Beta Composite Catalyst

Mn-Ce supported low temperature denitration catalyst and preparation method thereof

Ce(SO4)2/α-Fe2O3 selective catalytic reduction of NOx with NH3: preparation, characterization, and performance

High Efficiency of Ce-Modified MnOx/TiO2-ZrO2-Based Low-Temperature Selective Catalytic Reduction Denitration Catalysts

Method for preparing denitrified catalyst through cobalt-manganese double-exchange molecular sieve

Synergistic Removal of NOx and VOCs from Flue Gas on Mn-Based Catalysts

Industrial furnace sulfur trioxide pre removing and denitration device and method

SCR denitration catalyst for marine diesel engine and preparation method thereof

Cu SSZ 13 molecular sieve based catalyst adopting core shell structure as well as preparation and application of catalyst

Satisfactory Anti-Interference and High Performance of the 1Co-1Ce/Mn@ZSM-5 Catalyst for Simultaneous Removal of NO and Hg0 in Abominable Flue Gas.

Significant Effects of Adding Mode on Low-Temperature De-NOx Performance and SO2 Resistance of a MnCeTiOx Catalyst Prepared by the Co-Precipitation Method

MnOx-CuOx cordierite catalyst for selective catalytic oxidation of the NO at low temperature

Satisfactory Anti-Interference and High Performance of the 1Co–1Ce/Mn@ZSM-5 Catalyst for Simultaneous Removal of NO and Hg 0 in Abominable Flue Gas