Abstract:This study focuses on promoting the low temperature performance of vanadium-based catalysts; for this, the SHS method was applied to synthesize a series of Ti0.9VxM0.1-xO2-delta catalysts. The performances of the catalysts (Ti0.9V0.1O2-delta, Ti0.9Mn0.05V0.05O2-delta, and Ti0.9Ce0.05V0.05O2-delta), were fully investigated with the temperature-programmed-reaction, which proved that these SHS catalysts with nanometer size had high activity over a broad temperature window of 150-400 degrees C. Compared with Ti0.9V0.1O2-delta, the substituted Catalysts, Ti0.9Mn0.05V0.05O2-delta and Ti0.9Ce0.05V0.05O2-delta, showed higher N-2 selectivity at high temperatures. The Ce substituted catalyst exhibited good resistance to H2O and SO2 poisoning at low temperatures. The structural and physical-chemical properties of catalysts were characterized comprehensively by BET, XRD, FTIR, TEM, EDX, XPS, and TPD. The XRD results indicated that the active components of V, Mn, and Ce were highly dispersed over the catalysts. The Mn substitution could enhance the Bronsted acid sites on the catalyst surface and accelerate the SCR reaction at low temperatures. The XPS shows that the Ce substitution led to high concentration of chemisorbed oxygen, which diminished the unselective oxidation of NH3 by O-2 to N2O, NO, or NO2 and resulted in superior N-2 selectivity. The active components of the catalysts, such as V, Mn, and Ce, mostly existed in the form of mixed-valence which was beneficial for the oxidation of NO to NO2. Furthermore, the SCR reaction mechanism over Ti0.9Ce0.05V0.05O2-delta catalyst was also examined using in situ DRIFTS. The results revealed that high active monodentate,e nitrate and bridging nitrate species as well as abundant ionic NH4+ (Bronsted acid sites) were the key intermediates in the SCR reaction since the ad-monodentate nitrate and bridging nitrate species disappeared quickly in the presence of NH3.

High Efficiency of Ce-Modified MnOx/TiO2-ZrO2-Based Low-Temperature Selective Catalytic Reduction Denitration Catalysts

Catalytic performance of MnO 2-CeO 2/Ti 0.25Zr 0.25Al 0.5O 1.75 monolith catalyst for low temperature selective catalytic reduction of NO with NH 3

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Promoting Metal Oxides–zeolite Electron Interaction on MnCeOx/HY Catalyst for Boosting Nitrogen Oxides Reduction

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Synergetic Promotional Effects Between Cerium Oxides and Manganese Oxides for Nh3-Selective Catalyst Reduction over Ce-Mn/Tio2

Improvement of Catalytic Activity over Mn-modified CeZrO, Catalysts for the Selective Catalytic Reduction of NO with NH3

Novel shielding and synergy effects of Mn-Ce oxides confined in mesoporous zeolite for low temperature selective catalytic reduction of NOx with enhanced SO2/H2O tolerance

Mechanistic and Performance Insights into Low-Temperature NH3-SCR Based on Ce-modified Mn-Ti Catalysts

Ce(SO4)2/α-Fe2O3 selective catalytic reduction of NOx with NH3: preparation, characterization, and performance

Enhancing the Deno Performance of MnO /Ceo2-Zro2 Nanorod Catalyst for Low-Temperature NH3-SCR by TiO2 Modification

Effect of Ceria Doping on Catalytic Activity and SO2 Resistance of MnOx /tio2 Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Effect of Metal Ions Doping (M = Ti4+, Sn4+) on the Catalytic Performance of MnOx/CeO2 Catalyst for Low Temperature Selective Catalytic Reduction of NO with NH3

Thulium Oxides Supported on MnCeTiOX Catalysts for Low-Temperature NH3-SCR of NOX

Influence of Mn/(Mn+Ce) Ratio of MnOx-CeO2/WO3-ZrO2 Monolith Catalyst on Selective Catalytic Reduction of NOx with Ammonia

Tungsten Modified MnOx–CeO2/ZrO2 Monolith Catalysts for Selective Catalytic Reduction of NOx with Ammonia

Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature

Selective Catalytic Reduction of NOx with NH3 over Mn, Ce Substitution Ti0.9V0.1O2−δ Nanocomposites Catalysts Prepared by Self-Propagating High-Temperature Synthesis Method

Low-temperature selective catalytic reduction of NO with NH3 over MnOx-CeO2/ZrO2-TiO2 monolith catalyst

Role of Cerium in Improving NO Reduction with NH 3 over Mn–Ce/ASC Catalyst in Low-Temperature Flue Gas