Ultrasonic Wave Assisted GMAW A novel method adds ultrasonic wave to provide an additional force to detach the droplet BY
Y. Y. FAN,C. L. YANG,S. B. LIN,C. L. FAN,W. G. LIU
2012-01-01
Abstract:Gas metal arc welding (GMAW) is one of the most widely used industrial welding methods, preferred for its high productivity. A continuous and consumable wire electrode is fed through a welding gun, making it well suited to semiautomatic or automatic welding applications. The wire electrode plays the roles of heat source and liquid filler metal. The manner in which the liquid metal transfers from the electrode to the weld pool is referred to as metal transfer mode. It is the most important feature of GMAW and plays a significant role in determining the welding process stability and weld quality (Ref. 1). There are three basic metal transfer modes: short-circuiting, globular, and spray (Ref. 2). These metal transfer modes show different arc stabilities, weld formation, spatter levels, and so on. Shortcircuiting transfer encompasses the lowest range of welding currents and voltages. The arc length is relatively short, and the droplet cannot transfer until it touches the weld pool. The small, fast-freezing weld pool produced by the short-circuiting transfer and its associated low heat input are suitable for joining thin materials. When the welding currents and voltages are slightly higher than that used in short-circuiting transfer, globular transfer can be achieved. The drop size is greater than the diameter of the welding wire, and the detachment is mainly controlled by gravity. When the welding current further increases to a higher level that is above a critical value called the “transition current,” transfer occurs in the form of relatively small drops that are transferred at the rate of hundreds per second. This transfer mode is spray transfer. The spray transfer mode can be further classified into drop spray and streaming spray, based on the droplet size. The diameter of the drop is equal or slightly larger than the welding wire in drop spray, while it is much smaller in streaming spray (Ref. 3). Both spray transfer modes are stable. However, in the streaming spray, small drops at a relatively high speed have a strong impact on the weld pool. The resultant weld formation is finger-shaped penetration, which is associated with poor mechanical properties (Ref. 4). The drop spray is generally characterized by uniform drop size, regular detachment, directional droplet transfer, and insignificant spatter, so it is a preferred process (Ref. 5). However, the current range for drop spray transfer is relatively narrow — less than 10 A (Ref. 6). Small variables of the welding condition can bring a normal current variation larger than the narrow current range, so it is hard to maintain the drop spray process. On the other hand, globular transfer is associated with instable arc, spatter, and unacceptable weld appearance. This is mainly brought by the large drop size and low transfer frequency. Suppose that an auxiliary force can be applied on the droplet, the drop size will be minimized and the metal transfer frequency will be increased. As a result, the globular transfer will be a more stable and continuous process, similar to the drop spray process. In an effort to solve the above problem, application of an auxiliary force on the droplet has been achieved in a number of ways. The pulsed GMAW method uses pulsed current. A peak current higher than the transition current is used to produce a powerful electromagnetic force to detach the droplet (Refs. 7–9). The peak current value and duration time can be modulated to control the electromagnetic force. The average current for spray transfer decreases, but the transition current is unchanged. A reliable feedback signal is necessary to control the peak current and duration time because of the narrow range of transition current (Refs. 10–12). By monitoring excited droplet oscillation, the downward momentum of the droplet has been employed to enhance droplet detachment in the pulsed GMAW process. The peak current can be lower than the transition current, and accidental detachment is prevented (Ref. 13). Then the oscillation process of the droplet is improved by modified current waveforms. The metal transfer rate is further improved, and the control system is simplified (Ref. 14). The double-electrode GMAW (DE-GMAW) process adds a gas tungsten arc welding (GTAW) torch to the GMAW system, and the bypass arc produces an extra electromagnetic force to detach the droplet (Ref. 15). Then the DE-GMAW has been further modified into dual-bypass GMAW by adding two bypass tungsten electrodes (Ref. 16). As a result, two extra electro-