Abstract:Chloride-induced corrosion of reinforcement has been recognized as one of the most predominant causes of structural degradation. In this paper, experimental and numerical investigation was conducted to study the degraded shear performance of reinforced concrete beam. The corrosion of reinforcements, crack patterns, and structural behaviors of corroded specimens with various corrosion levels accelerated by the impressed current method were analyzed. The test results indicated that the corrosion-induced crack patterns have a close relationship with the level of reinforcement corrosion. Moreover, an obvious degradation of shear performance of corroded RC beams in terms of initial stiffness, cracking loads, ultimate bearing capacity, post-peak behavior, and energy dissipation capacity was observed, which became more pronounced as the corrosion level increased. When a severe corrosion level (eta(a) >= 12%) was encountered, the failure mode could even be changed from the shear-compression failure into a much more brittle diagonal splitting failure. In parallel, to numerically simulate the propagation of the main diagonal crack faithfully, the extended finite element method (XFEM) specified with an exponential softening traction-separation relationship was adopted. Moreover, to investigate the effect of corrosion-induced bond degradation, a user-defined element (UEL) was also developed to represent the interfacial bond response. The reasonable agreement between the numerical simulation and experimental results proved the feasibility of the proposed approach. (C) 2020 Elsevier Ltd. All rights reserved.

Numerical Simulation Approach for Structural Capacity of Corroded Reinforced Concrete Bridge

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

Numerical Analysis of Ultimate Strength of Concrete Filled Steel Tubular Arch Bridges

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

Simplified Structural Deterioration Model for Reinforced Concrete Bridge Piers under Cyclic Loading 1

Developing a Three-Dimensional Finite Element Analysis Approach to Simulate Corrosion-Induced Concrete Cracking in Reinforced Concrete Beams

Simplified evaluation approach for corrosion of reinforced concrete structures based on numerical simulation

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Time-dependent reliability analysis of reinforced concrete beams subjected to bending and marine atmospheric environment

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Numerical Simulation of Partial-Interaction Load-Deflection Behavior of Corroded Reinforced Concrete Beams Based on a Segmental Approach and Evaluation of Reinforcement Corrosion Level

State-of-art of the Mechanical Behaviour of the Corrosion Reinforced Concrete Bridges

Coupled Effect of Loading and Environment of Concrete Bridge in Service Life

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Probabilistic Lifetime Assessment of Marine Reinforced Concrete with Steel Corrosion and Cover Cracking

Experimental Study on Bearing Capacity of Corroded Reinforced Concrete Arch Considering Material Degradation

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Spatial Variability-Based Corrosion Risk Assessment and Strategy of Repair and Maintenance for RC Structures

Prediction of service performance for RC bridge by considering the coupling effect of load-environment in service cycle

Residual strengths of reinforced concrete beams with heavy deterioration

Path probability model of corrosion-crack assessment for existing reinforced concrete structures