Service Life Prediction Of Reinforced Concrete In A Sea-Crossing Railway Bridge In Jiaozhou Bay: A Case Study
Zhe Li,Zuquan Jin,Tiejun Zhao,Penggang Wang,Lixiao Zhao,Chuansheng Xiong,Yue Kang
DOI: https://doi.org/10.3390/app9173570
2019-01-01
Abstract:Reinforced bar corrosion induced by chloride ingression is one of the most significant threats to the durability of concrete structures in marine environments. The concrete cover thickness, compressive strength, chloride diffusion coefficient, and surface defects of reinforced concrete in the Jiaozhou Bay sea-crossing railway bridge were measured. The temperature and relative humidity in the concrete and the loading applied onto the reinforced concrete were monitored. Based on the DuraCrete model, a revised model for the service life prediction of concrete structures was established, considering the effects of temperature and loading on the chloride diffusion coefficient. Further, the reliability indexes of the reinforced concrete box girder, pier, and platform, located in the marine and land sections, in relation to service lives lasting various numbers of years, were calculated. The measured and calculated results show that the mean cover thicknesses of concrete piers in the marine and land sections are 52 mm and 36 mm, respectively, and the corresponding standard deviations are 5.21 mm and 3.18 mm, respectively. The mean compressive strengths of concrete in the marine and land sections are 56 MPa and 46 MPa, respectively. The corresponding standard deviations are 2.45 MPa and 2.67 MPa, respectively. The reliability indexes of the reinforced concrete box girder and platform in the marine section, under the condition of a service life of 100 years, are 1.81 and 1.76, respectively. When the corrosion-resistant reinforced bar was used in the pier structure in the marine section, its reliability index increased to 2.01. Furthermore, the reliability index of the reinforced concrete damaged by salt fog in the land section was 1.71.