Abstract:The erosion damage of marine reinforced concrete (RC) structures is induced by the physical and chemical coupling effect including both abrasion damage by sediment-laden water flow and corrosion damage by salt-laden water flow. However, the comprehensive effects of the abrasioncorrosive damage on structural performance evaluation have not been considered, which will underestimate structural risk. In this paper, an evaluation method of surface deterioration and bearing capacity is established for marine RC structures under the spatiotemporal effect of erosion damage. The theoretical friction-impact abrasion model of concrete is derived using the energy conservation method. On this basis, using the theoretical friction-impact abrasion model and the numerical simulation method, the environmental action factors were analyzed when erosion damage appeared. The variations in abrasion damage rate are discussed related to changes in impact angle, the impact speed, and the sediment content when abrasion damage occurs at the concrete surface. The influence of multiple parameters on abrasion damage rate is gained by combining with the results obtained from the numerical simulation method. Then, erosion damage considering the coupling of corrosion damage and abrasion damage is introduced to quantify the surface deterioration and bearing capacity of RC structures based on the continuous integral method. The uncertainty analysis under abrasion times ranging from 0 to 30 years is conducted to verify the spatiotemporal effect of erosion damage on surface deterioration and bearing capacity of RC structures. The result establishes a good foundation for the failure analysis and diagnosis of marine RC structures.

Spatial Variability-Based Corrosion Risk Assessment and Strategy of Repair and Maintenance for RC Structures

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Simplified Structural Deterioration Model for Reinforced Concrete Bridge Piers under Cyclic Loading 1

Corrosion-crack path based probabilistic model to predict the durability behavior of RC components

Path probability model of corrosion-crack assessment for existing reinforced concrete structures

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Probabilistic Approach for Durability Design of Concrete Structures in Marine Environments

Probabilistic Lifetime Assessment of Marine Reinforced Concrete with Steel Corrosion and Cover Cracking

Influence of Erosion Damage on the Spatiotemporal Deterioration of Marine RC Structures

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Time-dependent reliability analysis of reinforced concrete beams subjected to bending and marine atmospheric environment

Modeling of Time to Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Experimental Investigation of Corrosion-Induced Cover Cracking in Reinforced Concrete Structures

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Reinforcement Corrosion-Induced Cover Cracking and Its Time Prediction for Reinforced Concrete Structures

Durability related environmental zonation and design methodology for marine RC structures

A Probabilistic Model For Corrosion Prediction Of Steel Reinforcement

A Simplified Method for Risk Assessment of Surface Damage of Marine Reinforced Concrete Structures

Service Life Evaluation of Marine Concrete Structures Considering Spatial and Temporal Characteristics: A Framework Based on Multi Training-Mcs-nls

The Model for Predicting the Remaining Service Life of Reinforced Concrete Bridges In-Service and Applicability

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures