Abstract:Steel corrosion is the major form of failure of durability of concrete structures. The durability monitoring for concrete structure and its repair research are two urgent and necessary tasks, and the former provides the basis for the latter. For concrete durability monitoring, with the development of corrosion processes, environmental factors in the concrete (saturation, temperature, and so on) and the corrosion rate changing will have an effect on steel corrosion polarization dynamics. This paper reviewed some widely used foreign durability monitoring sensors for the reinforced concrete, and discussed the negative and positive aspects of them. Also, this paper introduced some newly developed domestic sensors which may be more suitable used in extra high-humidity and low-humidity environment. For concrete durability restoration, the improvement of technique for reinforced concrete structure durability can be considered from three aspects "prevention", "resistance" and "treatment". As to the "treatment", electrochemical rehabilitation is regarded as the only effective method to stop steel corrosion. This paper reviewed the traditional repair and electrochemical method for the reinforced concrete, and introduced cathodic protection, realkalisation of reinforced concrete, electro-deposition method, electrochemical chloride extraction (ECE) and electro-migration anticorrosion technology. The effect and principle of these method were discussed. Most importantly, this paper put out the concept of bi-directional electro-migration rehabilitation (BIEM), and introduced the principle, research state and technical difficulties of BIEM.

State-of-art of the Mechanical Behaviour of the Corrosion Reinforced Concrete Bridges

Probability-Based Performance Degradation Model and Constitutive Model for the Buckling Behavior of Corroded Steel Bars

State-of-art of corrosion-induced cracking of reinforced concrete structures

Simplified Structural Deterioration Model for Reinforced Concrete Bridge Piers under Cyclic Loading 1

THE INFLUENCES OF CORROSION DAMAGE ON THE FATIGUE CRACK DEVELOPMENT OF CONCRETE STRUCTURES

State-of-the-art Review on the Bond Properties of Corroded Reinforcing Steel Bar

STATE OF ART OF RESEARCH ON DURABILITY OF COASTAL AND OFFSHORE REINFORCED CONCRETE BRIDGES

Evaluation of corrosion morphology on mechanical properties of reinforcing steel bars using numerical simulation and simplified analytical model

Mechanical Performance of Corroded Steel Bars in Concrete

EXPERIMENTAL INVESTIGATION AND DESIGN OF SEVERELY CORRODED REINFORCED CONCRETE BEAMS

Residual strengths of reinforced concrete beams with heavy deterioration

Effect of Corrosion on Bond Behavior and Bending Strength of Reinforced Concrete Beams

THE STATE OF THE ART OF CONCRETE STRUCTURE DURABILITY MONITORING AND RESTORATION

Cover Cracking Model in Reinforced Concrete Structures Subject to Rebar Corrosion

Data-driven Corrosion Failure Probabilistic Assessment Model for Reinforced Concrete Structures

Revised Chloride Diffusion Model of Concrete Bridge Near Coastal Areas and Its Application

Damage Analysis and Cracking Model of Reinforced Concrete Structures with Rebar Corrosion

Effect of Chloride-Induced Reinforcing Steel Corrosion on the Flexural Strength of Reinforced Concrete Beams

Couple Effect of Loading and Corrosion of Concrete Bridge in Service Life

SIMULATED RESEARCH ON CORROSION OF REINFORCEMENT IN CONCRETE UNDER CHLORIDE ENVIRONMENT

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures