Abstract:To evaluate the residual service performance of corroded high-tensile steel wires, a batch of in situ wires that had served for 13 years in the hangers of an arch bridge was investigated. Four types of corroded wires were derived from the in situ wires by placing them in the indoor environment for 1.5 years (Type A) or treating them in an alternate dry-wet environment for 0.25-1.5 years (Types B, C, and D). The mechanical properties of the corroded wires were investigated with tensile and fatigue tests, and the fracture characteristics were observed. Fatigue tests on Type A wires with different stress ranges were conducted, and the stress intensity factor range Delta K-p at the bottom of crack-initiation pits was analyzed. According to the S-N curve for Type A wires, the crack-propagation characteristics of steel wires were investigated. The linear elastic fracture mechanics (LEFM) approach was used to predict the residual life of corroded wires in two systems of arch bridges. The tests show that the ultimate strain of corroded wires decreased with an increase in degree of corrosion. The fatigue properties of wires were found to degrade significantly at the early corrosion stage, and the degradation rate slowed down with further development of corrosion. The correlation between the fatigue life and the stress intensity factor range DKp at the bottom of corrosion pits shows that larger pitting size tended to have shorter life under the same stress range, and fatigue cracks were difficult to initiate at the corrosion pits below the fatigue threshold. The crack-growth parameters of the Paris law identified from the S-N curve of Type A wires were m = 2.87, C = 8 x 10(-12) under the stress ratio R = 0.5. The residual life predicted by LEFM shows that in a dry environment, corroded wires with an initial pitting depth of 0.6 mm can serve for more than 30 years in arch-beam combination-system bridges, whereas they can only serve for 5 years in floating-system arch bridges.

Experimental Study on Bearing Capacity of Corroded Reinforced Concrete Arch Considering Material Degradation

Experimental Study and Residual Performance Evaluation of Corroded High-Tensile Steel Wires

Simplified Structural Deterioration Model for Reinforced Concrete Bridge Piers under Cyclic Loading 1

Study on Degradation Regularity of Bearing Capacity of RC Beams under Corrosive Conditions

Corrosion-Induced Cracking Propagation Of Rc Beams Subjected To Different Corrosion Methods And Load Levels

Cracking of Reinforced Recycled Aggregate Concrete Beams Subjected to Loads and Steel Corrosion

Approach for Analyzing the Ultimate Strength of Concrete Filled Steel Tubular Arch Bridges with Stiffening Girder

Corrosion-induced Shear Performance Degradation of Reinforced Concrete Beams

Mechanical Degradation of Reinforced Concrete Columns Corroded Under Sustained Loads

Residual strengths of reinforced concrete beams with heavy deterioration

Effects of Reinforcement Corrosion and Sustained Load on Mechanical Behavior of Reinforced Concrete Columns.

Prediction of Corrosion-Induced Crack Width of Corroded Reinforced Concrete Structures

EXPERIMENTAL INVESTIGATION AND DESIGN OF SEVERELY CORRODED REINFORCED CONCRETE BEAMS

Maintenance strategy and method of concrete arch bridges in life cycle ii: performance degradation analysis and repair reinforcement methods

Experimental study on the ultimate bearing capacity of damaged RC arches strengthened with ultra-high performance concrete

Performance of Reinforced Concrete Beams Corroded under Sustained Service Loads: A Comparative Study of Two Accelerated Corrosion Techniques

Effects of Corrosion on Compressive Arch Action and Catenary Action of RC Frames to Resist Progressive Collapse Based on Numerical Analysis

State-of-art of the Mechanical Behaviour of the Corrosion Reinforced Concrete Bridges

Analysis of the Existing Reinforced Concrete Rigid Frame Arch Bridge Strengthened with Arch and Cable System

Reinforced Concrete Multi-Rib Arch Bridge Strengthened by Changing Structural System

Performance of Corroded Reinforced Concrete Columns under the Action of Eccentric Loads