Abstract:The formation of a uniform Fe-Al inhibition layer with a proper thickness at steel interface during continuous hot-dip galvanizing process is a crucial issue for industrial production. The inhibition layer prohibits the nucleation and growth of brittle Fe-Zn intermetallic compounds which deteriorate the adhesion of the galvanizing coating and result in an inhomogeneous distribution of the coating. The inhibition layer was identified to be Fe2Al5 with some Zn dissolved in it. But Fe2Al5 inhibition layer was damaged with galvanized time increasing, will lose the inhibition to the Fe- Zn reaction. Nevertheless, there is no systematic and comprehensive investigation the causes of the inhibition layer is damaged. The aim of this work is to clarify the destabilization mechanism of Fe2Al5 inhibition layer. In the present study, the mass fraction of 0.2%Al was added into the zinc bath at 450 degrees C for hot dip galvanizing. SEM was used to observe the structure characteristics of the hot-dip galvanized coating. EDS was used to quantitatively analyze the micro area components of phases and also Used its line scan and mapping scan to qualitatively analyze the element change of the coating cross section. By means of the Miedema model and the Toop model, the thermodynamic values of the binary Fe-Al, Fe-Zn and ternary Fe2Al5Znx (eta) intermetallic compounds (IMC) in the coatings were calculated. The fundamental reason for the Fe-Zn reaction caused by Fe2Al5 destabilization with galvanized time increasing was analyzed. The results show that because Fe-Al IMC which is generate preferentially had more stable thermodynamic property than Fe-Zn IMC, the continuous Fe2Al5 intermetallic compound inhibition layer was produced preferentially at steel and zinc bath interface which inhibit the Fe-Zn reaction. However, with the galvanized time increasing, Fe2Al5 destabilization which led to the loss of inhibitory effect of Fe-Zn reaction and produced FeZn10 (delta). There are two kinds of destabilization mechanism of Fe2Al5 inhibition layer, one is that the local depletion of Al at Fe2Al5 and zinc bath interface result in erosion of Fe2Al5 by Zn and the formed Fe2Al5Znx caused the decrease of the systematic thermodynamic stability which led to erosion and decomposition of Fe2Al5 by Zn. At the same time, FeZn10 (delta) phase was produced between the Fe2Al5 and zinc bath interface. The phase transformation process can be described as: Fe2Al5 ->eta -> L+eta+delta -> L+delta. The other kind of destabilization mechanism is Zn diffused to the steel substrate by Fe2Al5 grain boundaries and directly produced 5 phase between Fe2Al5 and steel substrate interface, which caused outburst of Fe2Al5. The two kinds of Fe2Al5 destabilization mechanism are mutual coexistence and mutual competition, in particular conditions may be a mechanism to occupy absolute advantage.

Destabilization Mechanism of Fe-Al Inhibition Layer in Zn-0.2%Al Hot-Dip Galvanizing Coating and Related Thermodynamic Evaluation

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

The inhibition of MnO on Fe 2 Al 5 Zn x growth and associated three-dimensional nested phase distribution in the galvanized coating of high-Al low-Si dual phase steel

Mesoscale Investigation of Reaction–diffusion and Structure Evolution During Fe–Al Inhibition Layer Formation in Hot-Dip Galvanizing

Effects of Aluminum Concentration on the Formation of Inhibition Layer During Hot-Dip Galvanizing

Experimental Measurements and Kinetic Investigation of Fe-Al Alloy Layer During the Galvanizing Process

Understanding the Formation Mechanism of Al-Rich Interfacial Layer during Galvanizing of Cu Pre-coated High-Strength Steel Sheet

Effect of Strip Entry Temperature on the Formation of Interfacial Layer During Hot-Dip Galvanizing of Press-Hardened Steel

Growth Process and Mechanism of Hot-Dip Galvanised Zn–5Al Coating on Steel

Effect of Electrodeposited Ni Layer on the Galvanized Coatings of Reactive Steels

Interface reaction of high-strength low-alloy steel with Al–43.4Zn–1.6Si (wt.%) metallic coating

Effect of Mg on the Microstructure and Corrosion Resistance of the Continuously Hot-Dip Galvanizing Zn-Mg Coating

Interface Reaction Dynamics and Mechanism of Plain Carbon Steel in Liquid Zinc

Effect of the Interface Microstructure of Hot-Dip Galvanizing High-Strength Automobile Steel on Its Tensile Fracture Behaviors

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

The characteristics of Zn–5Al–2Mg coating on low carbon steel by two-step galvanizing method

The initial corrosion mechanism of hot-dipping Zn–Al–Mg alloy coating in chloride-containing solution

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Effect of Al Content on the Microstructure of Hot-Depped Zinc Coating on Hot Stamping Steel

Atomistic study of intermetallics of Fe-Al-Zn system and their interfacial properties

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating