Abstract:Bulk glassy Cu–Zr–Ti base alloys containing a small amount of Nb or Ta were found to exhibit high strength combined with significant plastic elongation. The glass transition temperature (Tg), crystallization temperature (Tx) and ΔTx(=Tx−Tg) of the Cu-based bulk glassy alloys are in the range of 719 to 731 K, 765 to 769 K and 46 to 44 K, respectively, for the Nb-containing alloy and 716 to 741 K, 752 to 780 K and 44 to 34 K, respectively, for the Ta-containing alloy. With increasing Nb or Ta content to 3 at% for the (Cu0.6Zr0.3Ti0.1)100−xMx alloys, the Young’s modulus, yield strength and compressive fracture strength increase from 114 to 121 GPa, 1785 to 2010 MPa and 2150 to 2250 MPa, respectively, and the plastic elongation shows a maximum of 1.8% at 1%Nb and 3.4% at 1%Ta. The 1%Ta alloy exhibited good combination of high fracture strength of 2250 MPa and large total elongation of 5.4%. The effectiveness of additional Nb or Ta on the increase in elongation and fracture strength is presumably due to the mixed state of atomic pairs with attractive and repulsive bonding natures among the constituent elements with significantly different atomic size mismatches. The success of forming the bulk glassy alloys with high strength and significant elongation is encouraging for future applications as high-strength type materials.

Effect of Nb Addition on Thermal Stability, Glass Forming Ability and Mechanical Properties of Zr-Based Bulk Amorphous Alloys

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Preparation And Thermal Stability Of Zr-Al-Ni-Cu-Nb Bulk Amorphous Alloy Matrix Composites

Tuning Glass Formation and Mechanical Properties of ZrCoAl(Nb) Bulk Metallic Glass with Nb Microalloying Process

Effects of adding niobium on microstructures and mechanical properties of ((Zr40Ti40Ni20)72Be28)100-Nb bulk metallic glasses

The effect of Nb addition on mechanical properties, corrosion behavior, and metal-ion release of ZrAlCuNi bulk metallic glasses in artificial body fluid

Glass-Forming Ability and Thermal Properties of Al70Fe12.5V12.5X5(X = Zr, Nb, Ni) Amorphous Alloys via Minor Alloying Additions

Effects of Nb Addition on Icosahedral Quasicrystalline Phase Formation and Glass-Forming Ability of Zr–Ni–Cu–Al Metallic Glasses

The Microstructural Characteristics and Mechanical Properties of Nb-16Si-22Ti-2Al-2Cr Alloys with Zr Addition

Effect of Nb in (La0.5ce0.5)(64-X)al16ni5cu15nbx (X=0-5) Bulk Metallic Glasses

Microstructures and Mechanical Properties of Cast Nb-Ti-Si-Zr Alloys

Effect of Nb Addition on the Glass-Forming Ability, Soft-Magnetic Properties and Mechanical Properties of CoFeNiBSiNb Bulk Glassy Alloys

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Effect of Ti addition on supercooled liquid region and glass forming ability of bulk amorphous Zr60Cu20Ni10-xAl10Tix alloys

Effect of Al addition on the mechanical property and irradiation resistance of NbMoZr-based medium-entropy alloys

Thermal Stability and Mechanical Properties of Bulk Glassy Cu-Zr-Ti-(Nb, Ta) Alloys

Formation of Ni–Nb–Zr–X (X = Ti, Ta, Fe, Cu, Co) Bulk Metallic Glasses

Nanocrystal composites in Zr–Nb–Cu–Al metallic glasses

An ab initio simulation and experimental studies of the glass-forming ability and properties of Al86Ni(14-x)Zrx (x = 1∼7) alloys

Formation of Fe60Co8Zr10Mo5W2B15 Bulk Amorphous Alloy and Influences of Subsequent Heat Treatment on the Properties

Effects of Ag addition on crystallization, microstructure and mechanical properties of Zr-Cu-Ni-Al-Ag bulk metallic glasses