Abstract:Ablation resistance of C/C-SiC composite prepared via Si-Zr alloyed reactive melt infiltration was evaluated using a facile and economical laser ablation method. Linear ablation rates of the composite increased with an increase in laser power densities and decreased with extended ablation time. The C/C-SiC composite prepared via Si-Zr alloyed melt infiltration presented much better ablation resistance compared with the C/SiC composite prepared by polymer infiltration and pyrolysis process. The good ablation resistance of the composite was attributed to the melted ZrC layer formed at the ablation center region. Microstructure and phase composition of different ablated region were investigated by SEM and EDS, and a laser ablation model was finally proposed based on the testing results and microstructure characterization. Laser ablation of the composite experienced three distinct periods. At the very beginning, the laser ablation was dominated by the oxidation process. Then for the second period, the laser ablation was dominated by the evaporation, decomposition and sublimation process. With the further ablation of the composite, chemical stable ZrC was formed on the ablated surface and the laser ablation was synergistically controlled by the scouring away of ZrC melts and evaporation, decomposition and sublimation process.

C/C-Zr-Si Composites Prepared by Alloyed Reactive Melt Infiltration

C/C–SiC Composite Prepared by Si–10Zr Alloyed Melt Infiltration

ZrC Modified Carbon/carbon Composites Using ZrSi2 and Zr-Cu Alloys As Reactive Infiltrating Materials: A Comparative Investigation

C/C–ZrC Composite Prepared by Chemical Vapor Infiltration Combined with Alloyed Reactive Melt Infiltration

C/C–SiC–ZrC Composites Fabricated by Reactive Melt Infiltration with Si0.87Zr0.13 Alloy

Laser Ablation Resistance and Mechanism of Si-Zr Alloyed Melt Infiltrated C/C-SiC Composite

Mechanical Properties and Ablation Behavior of C/C-ZrC and C/C-ZrC-SiC Composites Prepared by Precursor Infiltration and Pyrolysis Combined with Chemical Vapor Infiltration

Reaction kinetics and ablation properties of C/C–ZrC composites fabricated by reactive melt infiltration

Preparation, Ablation Behavior and Mechanism of C/C-ZrC-SiC and C/C-SiC Composites

Ablation Behaviour and Mechanical Performance of ZrB2-ZrC-SiC Modified Carbon/carbon Composites Prepared by Vacuum Infiltration Combined with Reactive Melt Infiltration

Microstructure and Ablation Property of C/C-ZrC Composites Manufactured by Reactive Melt Infiltration

C/SiC–ZrB2–ZrC Composites Fabricated by Reactive Melt Infiltration with ZrSi2 Alloy

Ablative Property and Mechanism of SiC-CuxSiy Modified C/C-ZrC Composites Prepared by a Rapid Method

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Ablation Properties of C/C-ZrC-SiC Composites

Microstructure and Ablation Behavior of SiC Coated C/C–SiC–ZrC Composites Prepared by a Hybrid Infiltration Process

Ablation Behavior of a C/C-ZrC-SiC Composite Based on High-Solid-loading Slurry Impregnation under Oxyacetylene Torch

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

Microstructure and Ablation Behaviors of A Novel Gradient C/C-Zrc-Sic Composite Fabricated by an Improved Reactive Melt Infiltration

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration