Abstract:The thermal stability of the dual phase AlCrFeCoNiCu 0.5 high entropy alloy thin films at up to 600 °C under vacuum was studied through detailed characterization. The evolution of microstructure and chemical composition was revealed by X-ray diffraction, transmission Kikuchi diffraction and transmission electron microscopy . Also, the mechanical properties were measured by nanoindentation . Although the crystalline phase of all the HEA thin films was BCC-dominated, the FCC phase fraction increased from 16.6% (as-deposited) to 28.1% (600 °C-annealed). The as-deposited films exhibited a columnar morphology with an average grain size of 106.1 nm for length and 31.3 nm for width and remained the columnar shape until 600 °C. The columnar grains showed an increasing tendency of size at 200 °C (221.3 nm and 45.6 nm for length and width) and 400 °C (283.9 nm and 56.2 nm). At 600 °C, the columnar grain size decreased to 211.8 nm in length and 59.3 nm in width. Concurrently, the occurrence of new equiaxed grains was observed with an average diameter of 42.4 nm. The reduction of columnar grain size and the formation of equiaxed grains at 600 °C were explained based on the energy dispersive spectroscopy. Although no preferential evaporation was found, the elemental distribution revealed the formation of two secondary phases, i.e., Cu-rich FCC phase and Cr-rich BCC phase. The nanoindentation results indicated that the mechanical properties increased as the increase of annealing temperature. The hardness and elastic modulus of 600 °C-annealed sample were 8.5 ± 0.3 GPa and 205.4 ± 3.5 GPa, respectively, which were 10.4% and 41.5% higher than those of the as-deposited thin film. These findings are critical for a fundamental understanding of the microstructure and properties change of the dual-phase HEA thin films in high working temperatures.

Structural Coarsening During Annealing of an Aluminum Plate Heavily Deformed Using ECAE

Annealing Behavior of Aluminium Deformed by Equal Channel Angular Pressing

EBSP Study of the Annealing Behavior of Aluminum Deformed by Equal Channel Angular Processing

Microstructural Parameter-Based Characterization of Annealing Behaviour in Metals Deformed to High Strains

Annealing behaviour and mechanical properties of severely deformed interstitial free steel

Annealing Behavior of Nanostructured Aluminum Produced by Cold Rolling to Ultrahigh Strains

Microstructure and mechanical properties after annealing of equal-channel angular pressed interstitial-free steel

Grain Refinement and Strengthening of an Aluminum Alloy Subjected to Severe Plastic Deformation through Equal-Channel Angular Pressing

Controlled Annealing of Sandwich-Structured Aluminum AA1050 for Optimized Combinations of Strength and Ductility

EBSD Analysis of Deformed and Partially Recrystallized Microstructures in ECAE-Processed Copper

The microstructural evolution of dual phase high entropy alloy thin films by annealing

Evolution of Microstructure and Texture During Recovery and Recrystallization in Heavily Rolled Aluminum

Microstructure Evolution and Cooperative Strengthening Mechanism of Copper–Aluminum Bimetal Continuous Equal Channel Angular Pressing-Annealing Process

EBSD-Based Techniques for Characterization of Microstructural Restoration Processes During Annealing of Metals Deformed to Large Plastic Strains

Deformation Temperature and Postdeformation Annealing Effects on Severely Deformed TiNi Alloy by Equal Channel Angular Extrusion

Microstructure evolution of the rolled tungsten during the current-assisted annealing treatment

The Influence of Annealing on the Microstructural and Textural Evolution of Cold-Rolled Er Metal

Effect of Residual Deformation Energy and Critical Heating Rate on Cubic Texture and Grain Growth Behavior of Severely Deformed Aluminum Foil

Structural Characterization of Binary Al-Cu Alloy Processed by Equal Channel Angular Pressing at Half of the Melting Point

Microstructure Evolution in High Purity Aluminum Single Crystal Processed by Equal Channel Angular Pressing (ECAP)

Microstructure evolution and mechanical behavior of a CoCrFeNiMn0.75Cu0.25 high-entropy alloy by thermo-mechanical treatment