Abstract:Diffusion and polymerization behaviour of styrene (St) in commercially. available high density polyethylene (HDPE) pellets were studied and HDPE/PS nanoblend pellets were synthesized. Both the diffusion and polymerization steps were carried out in water medium. At 70 - 90 degrees C, diffusion behaviour of St towards HDPE pellets showed features of Fickian Diffusion. The saturation values of diffused St were different at different diffusion temperatures, and higher diffusion temperature meant higher saturation value, higher diffusion rate and shorter time to reach the saturation value. The amount of the initiator BPO was important in view of PS content in the pellets. With 0. 5 wt% - 1 wt% BPO, PS content was 11 wt% when diffusion and polymerization were carried out at 90 degrees C, while the PS content increased to about 16 wt% when excess amount of BPO (5 wt%) was used. The diametrical distribution of PS was investigated by Micro Fourier Transform Infrared Spectroscopy, showing that PS appeared throughout the HDPE pellets. PS distributions along the diameters of the pellets showed similar "M" shape curves for HDPE/PS pellets synthesized with different amounts of BPO. The peaks of the curves appeared at 200 mu m area to the surface and were related to crystalline structure of HDPE pellets. The phase morphology of PS in the blend pellets were characterized by field emission scanning electron microscopy. Typical sea. island morphology was revealed with an average particle size of less than 100 nm. The HDPE/PS blend pellets were melt. processed into cylindrical bars. PS phases in the extrusion bars of the blend pellets synthesized with 0. 5 wt% BPO showed Ci Rice morphology, reflecting that PS particles were aggregating instead of coalescing during processing, and particle sizes were from tens of nm to 200 nm. The disperse PS phase and HDPE matrix had good interaction and the HDPE/PS bars did not break with elongation of 600% and showed higher tensile stress than pure HDPE bars, which meant that 0. 5 wt% BPO was fairly good condition for preparing HDPE/PS nanoblends or other modified HDPE materials.

Diffusion and Polymerization Behavior of Styrene in Polypropylene Pellets of Different Aggregation State

Diffusion and Polymerization Behavior of Styrene in Polyethylene Pellets of Different Molecular Structures

Compatibilizing Efficiency of Copolymer Precursors for Immiscible Polymer Blends

Polymerization Kinetics of Styrene in Isotactic Polypropylene Pellets and Evolution of Phase Morphology During Polymerization

Diffusion and Polymerization Behavior of Styrene in High Density Polyethylene Pellets

Polypropylene/Polystyrene Blends Prepared by Diffusion and Subsequent Polymerization in Polypropylene Pellets after Injection Molding

Preparation of POE/PS Blends with Fine Particle Sizes by Diffusion and Subsequent Polymerization of Styrene in POE Pellets

Morphology, thermal behavior, rheological, and mechanical properties of polypropylene/polystyrene blends based on elongation flow

Preparation of Pp/Poe/Ps Ternary Alloys Via Diffusion and Polymerization of Styrene in Pp/Poe Alloys

Preparation of Polypropylene/Poly（styrene-co-（butyl Methacrylate）） Nanoblends by Diffusion and Subsequent Copolymerization of Monomers in Isotactic Polypropylene Pellets

Preparation and properties of polypropylene modified by grafting styrene

Morphology stabilization of the polypropylene/polystyrene nanoblends prepared by diffusion and polymerization of styrene in isotactic polypropylene pellets during melt mixing by the incorporation of divinylbenzene

Preparation of Isotactic Polypropylene/Polystyrene Blends by Diffusion and Subsequent Polymerization of Styrene in Isotactic Polypropylene Pellets

Mechanism and Process of the Redispersion of the Aggregated Nano-Sio2 Particles During Emulsion Polymerization of Styrene

Control of Surface Morphology of Polypropylene/polystyrene Blend Pellets Prepared by Diffusion and Subsequent Polymerization of Styrene in Isotactic Polypropylene Pellets

Structure and Rheological Properties of the Products of Solid-State Graft Polymerization of Styrene in Annealed Polypropylene Reactor Granules

Water Absorption Characteristics of Different Polyamide Resins and Their Effects on the Diffusion and Polymerization of St Monomer

Synergistic effect of styrene and zinc dimethyldithiocarbamate on the properties of high melt strength polypropylene

Solid-state graft polymerization of styrene in spherical polypropylene granules in the presence of TEMPO

Effects of Stereo-Defect Distribution on the Crystalline Morphology and Tensile Behavior of Isotactic Polypropylene Prepared by Compression Molding Process

Synthesis of Polypropylene- Grafted Graphene and Its Compatibilization Effect on Polypropylene/ Polystyrene Blends