Study on Melt-Grafting of Maleic Anhydride Onto Polypropylene in the Presence of Styrene
ZHANG Cai-liang,FENG Lian-fang,XU Zhong-bin,WANG Jia-jun,GU Xue-ping
DOI: https://doi.org/10.3969/j.issn.1008-9357.2005.03.003
2005-01-01
Abstract:In the presence of styrene (St), the melting-grafting of maleic anhydride (MAH) onto polypropylene was conducted in Haake torque rheometer and twins screw extruder (TSE) respectively. In experiments the dicumyl peroxide (DCP) concentration, St concentration, MAH concentration, reaction time, reaction temperature and screw speed were varied respectively. Results show that with the DCP concentration increasing, both the grating degree of MAH and melt flow index (MFR) of the grafted product increase at first and then deerease. When maintaining MAH concentration and increasing St concentration, the grafting degree of MAH reaches maximum at St:MAH=1mol?mol?1 and MFR always keeps decreasing. When maintaining St concentration and increasing MAH concentration, the grafting degree of MAH increases at first and then slightly decreases, and during which the MFR has a maximum point. With the reactive time increasing, both the grating degree of MAH and MFR of the grafted product increase at first and then decrease. When temperature is too high, the grafting degree of MAH decreases and the scission of the grafted product increases. When screw speed is low, the grating degree of MAH is low too, and when screw speed is high, the scission of the grafted product increases. The grafting of MAH in TSE is lower than that in Haake torque rheometer, while MFR of the grafted product in TSE is much lower than that in Haake torque rheometer. Based on the mechanism of melt-grafting, the above experimental results were discussed and explained.