Solid Phase Graft Polymerization of Styrene in Spherical Polypropylene Granules
YZ Zhang,ZQ Fan,Z Liu,YQ Zhang,LX Feng
DOI: https://doi.org/10.3321/j.issn:1000-3304.2002.04.006
2002-01-01
Acta Polymerica Sinica
Abstract:Spherical polypropylene (PP) granules of high porosity were synthesized using a spherical high yield TiCl4/MgCl2 supported catalyst. As much as 50 wt% of styrene (St)/benzoyl peroxide (BPO) mixture (based on PP weight) was adsorbed into the PP granules, and solid phase graft polymerization of St was conducted under different conditions. Effects of various reaction parameters, such as St/PP weight ratio, BPO/St ratio, reaction temperature, and reaction time on the amount of grafted PS in PP,graft efficiency,and the molecular weight of product were investigated. The structure and phase morphology of the produced PP/PP-g-PS alloy was characterized by infrared (FTIR) differential scanning calorimetry (DSC), GPC, viscometry and polarized microscope (PLM). The results showed that solid phase graft polymerization of St in PP granule produced PP/PP-g-PS/PS alloy with high amount of grafted PS (maximum 24.3 wt% of PS based on PP/PP-g-PS) and high graft efficiency (maximum 56.7%). The size of PP crystals was greatly reduced after grafting PS on PP. The final product is, still in the form of regular spherical granules, which is beneficial to industrial process. Under the studied conditions, there was slight degradation of the PP chains in the graft reaction.