Abstract:This study aims to explore the influence mechanism of interfacial reaction in BF. The interfacial reaction behavior was analyzed, the thermodynamic and evolution processes of interfacial reaction were studied, and the influence of interfacial reaction on BF was discussed. The results show that: The desulfurization reaction mechanism can be considered as the electron transfer at slag-iron interface. The viscosity of molten iron shows a decreasing trend with the increase of sulfur content, and the surface tension of molten iron will rapidly decrease with sulfur content, so the interfacial reaction rate will be accelerated. The reduction of FeO occurs at slag-carbon interface, the content of FeO in slag often shows a decreasing trend along the height direction of BF, the erosion rate of carbon brick will increase under the condition of slag with high FeO content. The reduction of SiO 2 is achieved with the help of two gas-phase compounds SiO and SiS. The average Si content in molten iron decreases with the increase of BF volume, which indicates that the large BF is more conducive to achieving low-carbon smelting. The reduction of TiO 2 is carried out at the slag-carbon interface step by step, the valence state of Ti element gradually decreases. The iron-carbon interface in hearth has a significant effect on the erosion of carbon brick and the state of hearth. The wetting and erosion process at iron-carbon interface is clarified based on the cycle model, the carbon brick is eroded in this cycle. The time for the carburization of molten iron is limited, so the carbon content of molten iron cannot reach saturation, although there are a large number of iron-carbon interfaces in hearth. The change trend of maximum temperature on sidewall is opposite to the actual carbon content, the change in carburization behavior at iron-carbon interface is the essential reason for the fluctuation of erosion rate of carbon brick.

Erosion of BF slag to different Zeta value beta Sialon and the fractal dimension of reaction interface

Erosion of BF slag to different Z-value β-sialon and the fractal dimension of reaction interface

Corrosion Behavior of BF Slag to SiAlON Bonded Corundum Refractories

Preparation and blast furnace slag corrosion behavior of SiC–Sialon–ZrN free-fired refractories

Corrosion Behavior Of Bf Slag To Sialon-Al2o3-Sic Composite Refractories

Study On The Slag Corrosion Resistance Of Unfired Al2o3-Sic/Beta-Sialon/Ti(C, N)-C Refractories

Erosion Behavior and Mechanism of Boronised Steels

Slag Corrosion Resistance of Al2O3-ZrN-Sialon-C Refractories

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Interfacial reaction behavior in blast furnace and analysis of influence mechanism

The Study on the Interface Reaction Characteristics of Different Binary Slag, CaO – MgO, Al2O3 – CaO, Al2O3 – MgO, SiO2 – CaO, SiO2 - MgO

Study on oxidation dynamics of different Z value beta Sialon

Effect of slag basicity on the interfacial wetting behavior between CA6 refractories and CaO–SiO2–MgO–Al2O3 based slag

Erosion behavior between CaCl2 and beta-sialon-SiC composite used for blast furnaces

Effect of Si and Prolonged Time on Interfacial Morphologies and Cavitation Erosion Behavior of Directionally Solidified Fe-B Alloy in Flowing Liquid Zinc

The Fractal Research on Low Silicon Sinter

Effects of Erosion Angle on Erosion Properties of Fe-B Alloy in Flowing Liquid Zinc

Reaction Sintered Fe–Sialon Ceramic Composite: Processing, Characterization and High Temperature Erosion Wear Behavior

Experimental Study on Flow Properties of Blast Furnace Slag with Different Alumina Contents Based on the Image Measurement Method

Erosion behavior between CaCl2 and β-Sialon -SiC composite used for blast furnaces

Research on Slag‐resistance of ZrN‐SiAlON‐SiC‐C Composite Refractory in Different Atmospheres