Abstract:Al2O3–Cr2O3 refractories have excellent slag corrosion resistance and can adapt to the oxidation/reduction atmosphere in the smelting reduction ironmaking furnace. Improving the corrosion resistance of chrome corundum refractories is of great significance for extending the life length of industrial kilns and decreasing carbon emissions. In this work, the influences of ZrO2 content on the phase evolution, microstructure, physicochemical properties, mechanical properties and slag corrosion resistance of the ZrO2 reinforced Al2O3–Cr2O3 composite refractories were investigated. The results show that the ZrO2 reinforced Al2O3–Cr2O3 composites are primarily composed of (Al, Cr)2O3 solid solution and m-ZrO2. The compressive strength, flexural strength and hardness of the composite refractories can be improved by adding 2.5 wt% ZrO2. However, adding more ZrO2 will reduce its mechanical properties. This is due to ZrO2 excessive content will augement the porosity of the composite refractories, and the phase transformation of ZrO2 will also lead to the formation of microcracks during the cooling process. It is worth noting that higher ZrO2 content improves the thermal shock resistance of the composites, which is primarily put down to the microcrack toughening mechanism of ZrO2. The corrosion tests show that the thicknesses of the corrosion and infiltration layers of composite refractories are significantly decreased accompanied by ZrO2 content increase. This is because the formation of high melting point CaZr4O9 reduces the CaO content and slag alkalinity, and inhibits the dissolution of Al2O3 into the slag to a certain extent. Therefore, the slag corrosion/penetration resistance of the of the composites are obviously improved with the increase of ZrO2 addition.

Slag Corrosion Resistance of Al2O3-ZrN-Sialon-C Refractories

Microstructure, phase evolution, mechanical properties and slag corrosion resistance of ZrO2 reinforced Al2O3–Cr2O3 composites

Microstructure evolution, mechanical characteristics and erosion behavior of Cr2O3–Al2O3–MgO–ZrO2 refractories in molten reduction slag

Corrosion mechanism of Al2O3–SiC–C refractory by SiO2–MgO-based slag

Corrosion Behavior of BF Slag to SiAlON Bonded Corundum Refractories

Corrosion Mechanism of Alumina-Chromia Refractory by SiO2-Al2O3-CaO Based Slag from Iron Capture Process of Spent Automotive Catalyst

Improved slag corrosion resistance of MgO–C refractories with calcium magnesium aluminate aggregate and silicon carbide: Corrosion behavior and thermodynamic simulation

Corrosion mechanism of novel MgO–Al3BC3 refractories in contact with converter slag

Research on the Wetting and Corrosion Behavior Between Converter Slag with Different Alkalinity and MgO-C Refractories

Preparation and Slag Erosion Resistance Mechanism of MgAlON Based Composite Refractories Synthesized from Solid Waste

Research on the Corrosion Behavior of Low Carbon Mold Flux on Submerged Nozzle Refractory

Corrosion mechanism of cement-bonded Al2O3–MgAl2O4 pre-cast castables in contact with molten steel and slag

Dissolution of Al2O3–C bricks in 45 wt% CaO-45 wt% SiO2-x wt% CaF2-(10-x) wt% Na2O slag

Effects of Cr2O3 Content on Microstructure and Mechanical Properties of Al2O3 Matrix Composites

Effect of Al2O3 on the Molten Slag Microstructure Information by Molecular Dynamics Simulation and Experimental Analysis

Numerical Understanding on Penetration and Corrosion Behavior of CaO–Al 2 O 3 –meo Slag to Al 2 O 3 –mgo Refractory

Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites

Corrosion in high alumina refractory serviced in a bench-scale entrained flow gasifier

Corrosion resistance of BN–ZrO2 ceramics with different additives by molten steel

Corrosion behavior of CaO–Al2O3–SiO2–MgO-Cr2O3 slag on MgO refractory brick for smelting of chromite

Enhanced performance of low-carbon MgO–C refractories with nano-sized ZrO2–Al2O3 composite powder