Effect of Molar Ratio on the Microstructure, Dielectric and Multiferroic Properties of Ni0.5Zn0.5Fe2O4-Pb0.8Zr0.2TiO3 Nanocomposite
Ruicheng Xu,Zhenhua Wang,Rongli Gao,Shilong Zhang,Qianwei Zhang,Zhendong Li,Chunyue Li,Gang Chen,Xiaoling Deng,Wei Cai,Chunlin Fu
DOI: https://doi.org/10.1007/s10854-018-9712-x
2018-01-01
Journal of Materials Science Materials in Electronics
Abstract:In the present work, Ni0.5Zn0.5Fe2O4/Pb0.8Zr0.2TiO3 nanocomposite with different molar ratio (1: 2, 1: 3, 1: 5, 1: 7) was prepared by hydrothermal method and sol–gel method, and the effect of molar ratio on the microstructure, dielectric and multiferroic properties was systematically investigated. X-ray diffraction and transmission electron microscopy analysis reveal inhomogeneous structures with isolated ferrite embedded into the ferroelectric (FE) matrix. Both the dielectric constant and the loss decrease firstly, and then increase with the increase of molar ratio, which is caused by the different microstructures and the formation of impurity phase. The dielectric resonance peak decreases firstly and then increases with increasing molar ratio, which is based on FE phase transition of Pb0.8Zr0.2TiO3 tuned by the magnetic phase. Among them, the nanocomposite with the molar ratio of 1:5 shows better FE properties and the lowest leakage current density, the saturation polarization, remnant polarization and coercive field are 3.74, 1.51 µC/cm2 and 7.93 kV/cm, respectively, at the measure frequency of 2 kHz. Unexpectedly, the magnetization first decreases and then increase with the increase of molar ratio, this abnormal behavior may be the result of the interface coupling effect between magnetic and FE phases. Also, this high sensitivity of multiferroic properties towards the molar ratio between magnetic and FE phases can be applied to the application in magnetoelectric devices.