A Comparative Study on the Structural, Dielectric, Ferroelectric and Magnetic Properties of CoFe2O4/PbZr0.52Ti0.48O3 Multiferroic Composite with Different Molar Ratios
Chunyue Li,Ruicheng Xu,Rongli Gao,Zhenhua Wang,Gang Chen,Xiaoling Deng,Wei Cai,Chunlin Fu,Qingting Li
DOI: https://doi.org/10.1088/2399-6528/ab5ea8
2019-01-01
Journal of Physics Communications
Abstract:Magnetoelectric composites have attracted much attentions due to their excellent multiferroic properties at room temperature. In this paper, CoFe2O4-PbZr0.52Ti0.48O3 (CFO-PZT) composite ceramics with different molar ratios (CFO/PZT = 1:4, 1:5, 1:6 and 1:7) were prepared by conventional solid reaction method. Effects of molar ratio on the structure, dielectric, ferroelectric and magnetic properties were comparatively investigated. X-ray diffraction patterns confirmed biphase structures of the composites, which can be indexed as CFO and PZT, no other obvious phase can be found with the limitation of theXRDresolution. Scanning electron microscopy (SEM) images show that the surface of the prepared samples is not dense enough and many pores are formed, the mean grain size is about 200 nm. The same relaxation behavior was observed in the intermediate temperature range of PZT-CFO composite ceramics. At room temperature, the dielectric constant and dielectric loss of the specimen 1:4 are the highest. The leakage current of the sample 1:4 is the lowest while the sample 1:6 has the largest value. As theCFO content in the composite decreases, both the saturation (Ms) and the remnant (Mr) magnetization decrease. Among them, the sample 1:4 presents better ferroelectric and magnetic properties, the remnant polarization is 1.13 mu C cm(-2), the saturation magnetization and remnant magnetization are 11.01 and 3.28 emu g(-1), respectively. The sample 1:6 has the largest coercive field (945.27 Oe) while the sample 1:7 show the smallest value (681.19 Oe). Interface interaction between CFO/PZT may be applied to explain this phenomenon.