Magnetoelectric effects of nanoparticulate Pb(Zr0.52Ti0.48)O3-NiFe2O4 composite films

Hyejin Ryu,P. Murugavel,J. H. Lee,S. C. Chae,T. W. Noh,Yoon Seok Oh,Hyung Jin Kim,Kee Hoon Kim,Jae Hyuck Jang,Miyoung Kim,C. Bae,J.-G. Park

DOI: https://doi.org/10.1063/1.2338766

2006-06-28

Abstract:We fabricated Pb(Zr0.52Ti0.48)O3-NiFe2O4 composite films consisting of randomly dispersed NiFe2O4 nanoparticles in the Pb(Zr0.52Ti0.48)O3 matrix. The structural analysis revealed that the crystal axes of the NiFe2O4 nanoparticles are aligned with those of the ferroelectric matrix. The composite has good ferroelectric and magnetic properties. We measured the transverse and longitudinal components of the magnetoelectric voltage coefficient, which supports the postulate that the magnetoelectric effect comes from direct stress coupling between magnetostrictive NiFe2O4 and piezoelectric Pb(Zr0.52Ti0.48)O3 grains.

Materials Science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore and verify the magnetoelectric effect of Pb(Zr\(_{0.52}\)Ti\(_{0.48}\))O\(_3\) (abbreviated as PZT) and NiFe\(_2\)O\(_4\) (abbreviated as NFO) composite films composed of nanoparticles. Specifically, the author hopes to confirm whether the magnetoelectric effect in this composite material comes from the direct stress coupling between ferromagnetic NFO particles and piezoelectric PZT matrix.

### Main research questions:
1. **Source of magnetoelectric effect**: Verify whether the magnetoelectric effect indeed comes from the direct stress coupling between NFO and PZT.
2. **Microstructure optimization**: By dispersing NFO in the form of nanoparticles in the PZT matrix instead of forming nanopillars, reduce the possible leakage current paths, thereby improving the performance of the material.
3. **Performance evaluation**: Measure and compare the transverse (αE31) and longitudinal (αE33) magnetoelectric voltage coefficients of the composite film to evaluate the specific manifestation of its magnetoelectric effect.

### Research methods:
- **Material preparation**: A 0.65PZT - 0.35NFO composite film was prepared on an Nb - doped SrTiO\(_3\) substrate by pulsed - laser deposition (PLD).
- **Structural analysis**: The crystal orientation and microstructure of the film were studied by X - ray diffraction (XRD) and transmission electron microscopy (TEM).
- **Performance testing**: The ferroelectricity and magnetism of the composite film were measured, and the magnetoelectric voltage coefficient αE was measured by a self - made device.

### Results:
- The composite film exhibits good ferroelectric and magnetic properties.
- The measured magnetoelectric voltage coefficients αE31 are approximately 4 mV/cm Oe, and αE33 are approximately 16 mV/cm Oe.
- The experimental results show that the magnetoelectric effect indeed originates from the coupling between the magnetostrictive effect of NFO and the piezoelectric effect of PZT.

Through these studies, the author has successfully demonstrated the magnetoelectric effect of the PZT - NFO composite film and provided important experimental basis for further optimizing this type of composite material in the future.