Microstructure and wear-resistance performance of WC / Cu-Ni-Mn composite coatings

Xuewei Meng,Weisheng Xia,Shuai Yang
2017-01-01
Abstract:The Cu-Ni-Mn alloy matrix coatings reinforced by WC particles (WC/Cu-Ni-Mn) are deposited on a steel substrate by a manual oxyacetylene weld. Microstructure and wear resistance performance of the fabricated coatings are investigated. There are no cracks or other defects observed in the hardfacing coating. Uniformly distributed WC particles in the composite hardfacing coating are not dissolved, and its volume fraction is up to about 63%. A sound interfacial junction form between the WC particles and the Cu-Ni-Mn alloy metal matrix binder. Under threebody abrasion testing with silica sands, the coatings shows about 4 times better wear resistance performance than the high-Cr cast iron. The main wear mechanisms are the plastic extrusion of the Cu-Ni-Mn matrix and the fracturing of WC-reinforcement particles under three-body abrasive wear. The wear behavior of the coatings also is investigated. At room temperature, the sliding wear-resistances of the as-deposited WC/Cu-Ni-Mn coatings is 1.83 higher than the commercial Fe-Cr-C hardfacing coating which is mainly ascribed to the high volume fraction and uniform distribution of WC in the Cu-Ni-Mn metal matrix. At 350 °C in air, the relative wear-resistance values is 1.90, owing to the good thermal stability of WC. The main sliding wear mechanisms of the coatings are adhesion and abrasion. Besides,the wear also is influenced by metal matrix softening at 350 °C.
What problem does this paper attempt to address?