Abstract:In the microelectronics industry the flip-chip (FC) technology is broadly used to enhance the packaging density. However, the small size and the unique geometry of the FC solder joints induce the electromigration (EM) reliability issue. In this study, a pair of lead-free solder joints (SAC1205) was EM tested by a current of 7.5 103 A/cm2. During the tests, X-ray laminography was applied to observe the microstructure evolution in-situ. Laminography enables the non-destructive observation of the bump microstructure and allows for a quantitative three-dimensional (3D) analysis. After EM testing for 650 h, a new EM failure mechanism was found, differing from the two well-known models, the pancake void propagation and the under-bump-metallization dissolution. Here, a few pre-existing small voids grew and simultaneously many new voids formed and grew over the entire EM testing period. Most of the nucleating voids were distributed in the current crowding region, a few also located in the low-currentdensity region. As the testing time increased, voids increasingly coalesced with each other, forming a porous network which occupied a large part of the interface area and caused the EM failure. A finiteelement (FE) method was then applied to analyze the interplay between the microstructure evolution and current density redistribution. A series of 3D FE models was built based on the laminography images for the different testing stages. The current density distribution from the FE analysis indicates that the formation of discrete voids did not affect the global current density distribution until a major coalescence of the voids occurred. The relieving of the global current crowding in the pancake void model was not found in this new EM failure mechanism. It was the local current crowding around individual void found in the new mechanism that is held responsible for the EM retardation. © 2016 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Design of experiments of electromigration reliability for solder joints of a wafer level chip scale package

A new prediction methodology for electromigration-induced solder degradation in a WL-CSP system

Prediction of Electromigration Failure of Solder Joints and Its Sensitivity Analysis

Electromigration reliability evaluation in FCBGA package based on orthogonal experimental design

Computational Analysis of Mechanical and Electromigration Reliability Problems

Dynamic Substructure Method for Prediction of Solder Joint Reliability of IC Package under Drop Test

Electromigration Time to Failure Simulation for Solder Bumps of a Chip Scale Package

DESIGN OF EXPERIMENTS AND SENSITIVITY ANALYSIS FOR ELECTROMIGRATION ON SOLDER JOINTS

Study of Electromigration-Induced Formation of Discrete Voids in Flip-Chip Solder Joints by In-Situ 3D Laminography Observation and Finite-Element Modeling

The Study of the Reliability of Complex Components during the Electromigration Process

Impact of geometry parameter on electromigration reliability in FCBGA package

Electromigration Mechanism of Failure in Flip-Chip Solder Joints Based on Discrete Void Formation

MODELING OF ELECTROMIGRATION FAILURE PREDICTING FOR FCBGA SOLDER BUMP UNDER MULTI-PHYSICAL FIELD LOADS

Impact of the UBM geometry and solder bump shape on electromigration reliability in a package system

Comparison of the Time-Dependent Physical Processes in the Electromigration of Deep Submicron Copper and Aluminum Interconnects

Study of discrete voids formation in flip-chip solder joints due to electromigration using in-situ 3 D laminography and

The Effect of Micro-Structure Evolution in Electromigration on the Reliability of Solder Joints

Study of electromigration-induced formation of discrete voids in flip-chip solder joints by in-situ 3 D laminography

Investigation on electromigration failure behavior of SAC305/SnPb micro-hybrid solder joints for package-on-package techniques: Experiment and simulation

The Effect of Atomic Density Gradient in Electromigration

Prediction Of Electromigration Induced Voids And Hillock For Ic Interconnect Structures