Abstract:For microelectronic industry, Cu-based substrate and epoxy molding compound (EMC) interface is inherently weak and most likely to delaminate, well-known as a major threat for integrated circuits (ICs) reliability. In this paper, hierarchical whisker-like oxide/Cu cone structure was for the first time to be fabricated by combining electroless plating with heat treatment methods to enhance the interface adhesion between Cu-based substrate and EMC. The surface morphology was characterized by scanning electron microscope (SEM). Result shows that the hierarchical whisker-like oxide/Cu cone film is fine, dense and uniform; Single Cu cone structure is about 3-5 μm in height and 1 μm in root diameter; a layer of whisker-like oxide grows perpendicularly to circular surface of Cu cone, with length ranging from tens to hundreds of nanometers. Adhesion strength between the as-prepared substrates and EMC were measured by button shear test. With consideration of oxidation caused by practical processes (e.g. wire bonding), the interface of EMC and porous oxide formed at 260°C for 5 min was taken as standard sample, representative of practical interface. To further study the effect of whisker-like oxide and Cu cone solely on adhesion performance, whisker-like oxide, porous oxide/Cu cone were investigated as well. Button shear test results reveal that interfacial adhesion strength of EMC and whisker-like oxide, porous oxide/Cu cone, hierarchical whisker-like oxide/Cu cone are 85%, 110% and 162% higher than that of standard interface. Moreover, the mechanism for adhesion improvement was discussed by facture surface observation, failure path assumption and force-displacement curve analysis. Results show that interface of EMC and hierarchical whisker-like oxide/Cu cone exhibits brittle/ductile property with about 3-5 μm thick EMC left on the fracture surface, indicating cohesive failure caused by remarkable mechanical interlocking effect. © 2011 Elsevier Ltd. All rights reserved.

Influence of Current Density on the Interfacial Bond Strength of Electroformed Layers

Adhesion improvement of Cu-based substrate and epoxy molding compound interface by hierarchical structure preparation

Effect of High-Frequency and High-Density Current on Adhesive Strength of Copper Thin Film

Theoretical Derivation of the Effect of Bonding Current on the Bonding Interface during Anodic Bonding of PEG-Based Encapsulation Materials and Aluminum

Meniscus-confined Electrodeposition of Metallic Microstructures with In-Process Monitoring of Surface Qualities

Effect of the Thickness Uniformity in Micro-Electroforming Process by Dividing Conductive Zone on Cathode

A study on the effect of inter-electrode gap and pulse voltage on current density in electrochemical additive manufacturing

Interfacial adhesion between electrical contacts determined by surface quality

Measurement of Interfacial Toughness of Metal Film Wire and Polymer Membrane Through Electricity Induced Buckling Method

An investigation of methods to enhance adhesion of conductive layer and dielectric substrate for additive manufacturing of electronics

Current-carrying friction of Ag coatings by additive manufacturing: uncovering the role of electric current

Parameter Characterization of Anodic Bonded Electrical Interconnect in MEMS/NEMS Devices

Electrical interconnect in MEMS/NEMS devices by Au/a-Si eutectic reaction

Introduction of a Chemical-Free Metal PDMS Thermal Bonding for Fabrication of Flexible Electrode by Metal Transfer onto PDMS

Superior electroadhesion force with permittivity-engineered bilayer films using electrostatic simulation and machine learning approaches

Fabrication of high-aspect-ratio metallic microstructures by microelectroforming using silver-coated polydimethylsiloxane molds with controllable wettability

Study and Measurement of Micro-Scale Bonding Strength in Vertical Direction

A New Test Structure To Measure Bonding Strength In Micro-Bonding Area

Study on the Manipulation Strategy of Metallic Microstructures Based on Electrochemical-Assisted Method

Pulse electric current induced interfacial ductile phase on improving the mechanical properties of the Au20Sn/Cu solder joints