Abstract:Decarburization is an unwanted carbon-loss phenomenon on the surfaces of a material when they are exposed to oxidizing environments at elevated temperatures. Decarburization of steels after heat treatment has been widely studied and reported. However, up to now, there has not been any systematic study on the decarburization of additively manufactured parts. Wire-arc additive manufacturing (WAAM) is an efficient additive manufacturing process for producing large engineering parts. As the parts produced by WAAM are usually large in size, the use of a vacuum environment to prevent decarburization is not always feasible. Therefore, there is a need to study the decarburization of WAAM-produced parts, especially after the heat treatment processes. This study investigated the decarburization of a WAAM-produced ER70S-6 steel using both the as-printed material and samples heat-treated at different temperatures (800 °C, 850 °C, 900 °C, and 950 °C) for different durations (30 min, 60 min, and 90 min). Furthermore, numerical simulation was carried out using Thermo-Calc computational software to predict the carbon concentration profiles of the steel during the heat treatment processes. Decarburization was found to occur not only in the heat-treated samples but also on the surfaces of the as-printed parts (despite the use of Ar for shielding). The decarburization depth was found to increase with an increase in heat treatment temperature or duration. The part heat-treated at the lowest temperature of 800 °C for merely 30 min was observed to have a large decarburization depth of about 200 μm. For the same heating duration of 30 min, an increase in temperature of 150 °C to 950 °C increased the decarburization depth drastically by 150% to 500 μm. This study serves well to demonstrate the need for further study to control or minimize decarburization for the purpose of ensuring the quality and reliability of additively manufactured engineering components.

Surface Decarburization Behaviour of A Novel Die Steel

EXPERIMENTAL RESEARCH ON BEHAVIOR OF DECARBURIZATION FOR THE FLAT DIE STEELS AISI D2，M2 AND S5

Characterization of Surface Oxidation and Numerical Simulation of Oxidation Kinetics for Fe-3%Si Steel During Decarburization

Experimental and modelling research on the influence of different pre-decarburization microstructures of Fe-0.6C-1.8Si-0.8Mn spring steel

Effect of Surface Oxide on Decarburization Reaction in the Austenitic Steel S304HCu

Microstructural Stability and Softening Resistance of a Novel Hot-Work Die Steel

Study on Decarburization Mechanism and Law of GCr15 Bearing Steel during Heat Treatment

Experimental investigations on wear resistance characteristics of different die materials for advanced high-strength steel blanking in close section

A Study on the Die Steel Surface Modification by Electron Beam

Characterization of Hot Deformation Behavior and Processing Map of As-Cast H13 Hot Work Die Steel

Effect of dew point temperature on surface selective oxidation behavior of Cu-bearing high strength steel

Decarburization of Wire-Arc Additively Manufactured ER70S-6 Steel

High-temperature oxidation wear performance and mechanism of Cr–Mo (W)–V hot-work die steel

Effect of nitrided-layer microstructure control on wear behavior of AISI H13 hot work die steel

Effect of Tempering Temperature on Microstructure and Properties of a New Type of Nitrogen‐Containing Hot‐Work Die Steel 3Cr7Mo2NiSiVN

High-temperature oxidation behavior and subsurface phase transformation of high-Mn high-Al steel

Effects of deep cryogenic treatment on the microstructure evolution, mechanical and thermal fatigue properties of H13 hot work die steel

Carbide Evolution for a Quenched and Tempered Dievar Steel

The Surface Integrity in Machining Hardened Steel Skd11 for Die and Mold

Optimizing the Morphology of Primary Carbides and Mechanical Properties during Processing Of Cast-Steel (Din Gx210crv12 1) Press-Forming Dies

Effect of surface finishing on the oxidation characteristics of a Fe-21Cr-32Ni alloy in supercritical carbon dioxide