Abstract:The mechanical properties of quench-tempered high-strength low-alloy steels are commonly optimized by fine and dispersively distributed alloy carbides. The role of the alloying elements in determining the alloy carbide precipitation sequence is of great significance. The co-addition of carbide-forming elements such as Mo, V and Nb complicates the precipitation behavior. The mutual inter-solutions and growth rates of various MC- and/or M2C-type carbides are qualitatively affected by the intrinsic solubility and diffusion at certain tempering condition. However, comprehensive study of the precipitation sequence must be followed with atomic scale resolution techniques. The 3D atom probe (3DAP) is a unique tool capable of obtaining chemical information at the atomic level, offering a powerful method to investigate microstructural and compositional changes occurring at nano-scale. And the sizes, morphology and composition of individual alloy carbide may be visualized and quantified by 3DAP. In this paper, a quenched Nb-V microalloyed steel was chosen to investigate the precipitation behavior of alloy carbide after tempering at 450-650 V for different times. 3DAP, micro-hardness test and TEM were applied to characterize the phenomena of hardening and softening during tempering, and the composition evolution and growth behaviors of the alloyed carbides were also studied. The results indicated the second hardening of the 500-600 degrees C tempering martensite is mainly resulting from precipitation strengthening of alloy carbides. The alloy carbides composition dynamically changed with elevated temperature or prolonged time, that is, the stronger carbide-forming elements replaced or partly replaced the weaker ones. At first V and Nb replaced Mo, and then Nb partly replaced V, and at last the carbides with certain composition were formed. Tempering time has relatively less effect on the carbides composition compared with temperature. When the tempering temperature elevated or tempering time prolonged, the alloying elements can obtain adequate diffusion energy and/or time, the plate-like carbides preferentially grow along the radial direction, and then grow along the thickness direction and start to coarsen.

Carbide Evolution for a Quenched and Tempered Dievar Steel

Characterization of Carbide Precipitation During Tempering for Quenched Dievar Steel

Mechanical Properties and Thermal Stability of Carbide Dispersion Strengthened CLF-1 Steel

Evolution and Coarsening of Carbides in 2.25Cr-Lmo Steel Weld Metal During High Temperature Tempering

3D Atom Probe Characterazation of Alloy Carbides in Tempering Martenite Ii. Growth

Carbide precipitation during tempering of Hybrid Steel 60

Evolution Behavior of Carbides in 2.25Cr-1Mo-0.25v Steel

Carbide Precipitation Behavior of High‐Alloy Steel During Solidification and Cooling Process

Carbides Dissolution in 5Cr15MoV Martensitic Stainless Steel and New Insights into Its Effect on Microstructure and Hardness

Compositional and structural characterization of alloyed carbide by 3D atom probe and high-resolution TEM

EVOLUTION OF CARBIDE IN 25-12 AUSTENITIC HEATRESISTANT CAST STEEL DURING SERVICE

Evolution Behavior and Fracture Criterion of Carbides in D2 Cold‐Work Die Steel During Hot Working Process

Study on Diversified Carbide Precipitation in High‐Strength Low‐Alloy Steel during Tempering

Effect of Carbide Precipitation on Hardness and Wear Resistance of H13 Steel

Evolution of Carbides and Carbon Content in Matrix of an Ultra-High Carbon Sintered Steel During Heat Treatment Process

Rietveld Quantitative Analysis of Carbides Precipitation in Normalized-Tempered 2.25Cr-1Mo-0.25v Steel

3D ATOM PROBE CHARACTERAZATION OF ALLOY CARBIDES IN TEMPERING MARTENITE III. Coarsening

Influence Of Quenching-Tempering On The Carbide Precipitation Of 2.25cr-Imo-0.25v Steel Used In Reactor Pressure Vessels

M5C2 Carbide Precipitates in a High-Cr Martensitic Steel

Precipitate Phase Evolution in a 11cr Ferritic/Martensitic Steel During Tempering

Quenching and Tempering-Dependent Evolution on the Microstructure and Mechanical Performance Based on a Laser Additively Manufactured 12CrNi2 Alloy Steel