Abstract:To solve the problem of poor uniformity of microstructure of high alloy bearing steel G13Cr4Mo4Ni4V after rolling, the deformation behavior of the steel and its effect on the microstructure evolution was studied systematically. Gleeble-3800 thermo-mechanical simulator was used for precise control of deformation temperature ranging from 1000 to 1200 °C and deformation rate 0.01–10 s−1. Based on modified stress and strain curves by temperature and friction, the processing map of tested steel was drawn. Electron backscatter diffraction (EBSD) and transmission electron microscope (TEM) were used to analyze the typical microstructure and carbide properties of different hot working domains respectively. The results showed the processing map could be divided into four regions: domain A 1000–1150 °C, 0.1–10 s−1; B 1000–1100 °C, 0.01–0.1 s−1; C 1100–1150 °C, 0.01–0.1 s−1 and D 1150–1200 °C, 1–10 s−1. Domain A was characterized by incomplete dynamic recrystallization (DRX) which included fine recrystallized grains and elongated deformed grains, whose softening mechanism was mainly discontinuous DRX (dDRX) and limited DRV and continuous DRX (cDRV) related to the ferrites and carbides. For domain B, the deformed grains gradually disappear with temperature rising, instead serrated grains appear with dDRX as dominating softening mechanism. A large number of carbides hinder DRX at 1000 °C with low temperature. With the increase of temperature, carbides dissolve and DRX degree increases. Grain coarsening is obvious because of high deformation temperature and low strain rate in domain C, although the nanoscale MC type carbides prevent recrystallization grain coarsening to some extent. Completely DRX resulted in uniform and fine with defect-free deformation microstructure in domain D, whose volume fraction of recrystallization reached up to 0.96 according to EBSD results. By considering the uniformity of microstructure and the distribution of carbide comprehensively, domain D is an ideal region for hot working.

Evolution Behavior and Fracture Criterion of Carbides in D2 Cold‐Work Die Steel During Hot Working Process

Carbide Evolution for a Quenched and Tempered Dievar Steel

Study on Evolution Behavior of Carbides in Industrial‐Grade American Iron and Steel Institute M35 High‐Speed Steel Produced by Electroslag Remelting

Evolution and Coarsening of Carbides in 2.25Cr-Lmo Steel Weld Metal During High Temperature Tempering

Stress-strain behavior and microstructural evolution of ultra-high carbon Fe-C-Cr-V-Mo steel subjected to hot deformation

Effect of Carbides on Thermos-Plastic and Crack Initiation and Expansion of High-Carbon Chromium-Bearing Steel Castings

Dissolution Behavior of Eutectic Carbides in Medium-Alloy Steels for Heavy Forgings

High temperature fracture mechanism of ultrafine WC-Co cemented carbides containing (Ti,W)C

Carbides Dissolution in 5Cr15MoV Martensitic Stainless Steel and New Insights into Its Effect on Microstructure and Hardness

Transformation behavior of primary MC and M 2 C carbides in Cr4Mo4V steel

High-temperature oxidation wear performance and mechanism of Cr–Mo (W)–V hot-work die steel

Effect of Tempering Temperature on Microstructure and Properties of a New Type of Nitrogen‐Containing Hot‐Work Die Steel 3Cr7Mo2NiSiVN

Effects of Microstructure Evolution on Fretting Wear Behaviors of 25CrNi2MoVE Steel under Different Tempering States

Effect of Yttrium on Inclusion and Eutectic Carbide in D2 Cold Working Die Steel

Carbide Precipitation Behavior of High‐Alloy Steel During Solidification and Cooling Process

Characterization of Carbide Precipitation During Tempering for Quenched Dievar Steel

Study on Hot‐Compressive Deformation Behavior and Microstructure Evolution of 12Cr10Co3MoWVNbNB Martensitic Steel

Effects of deformation-induced martensitic transformation on cryogenic fracture toughness for metastable Si8V2Fe45Cr10Mn5Co30 high-entropy alloy

Formation and evolution of primary carbides in high-carbon martensitic stainless steel

Characteristics and transformation of primary carbides during austenitization in Cr4Mo4V bearing steel

Study on hot compressive deformation behavior and microstructure evolution of G13Cr4Mo4Ni4V steel