Abstract:Y2W3O12 particles with negative thermal expansion (NTE) can offset the high thermal expansion of Ag-based sealants, thus relieving the residual stress of electrolyte/interconnect joints in protonic ceramic fuel cell (PCFC) stacks. Nevertheless, violent interfacial reactions between Y2W3O12 particles and BaZr0.1Ce0.7Y0.1Yb0.1O3-delta electrolyte have severely restricted the application of these NTE particles. Herein, novel Y2W3O12@SiO2 composite particles with a core-shell structure are successfully designed to address this conundrum. The thermal expansion coefficient of Ag-based sealant is lowered from 19.7 to 14.6 ppm/K by adding 20 wt% Y2W3O12@SiO2 particles. During joining, the SiO2 shell significantly reduces the reaction consumption of Y2W3O12, fully exploiting its NTE properties. Meanwhile, a tiny portion of SiO2 participates in and regulates interfacial re-actions, generating mechanically matched reaction layers. Finite element simulation demonstrates that intro-ducing Y2W3O12@SiO2 particles significantly releases the compressive X-stress near the BaZr0.1Ce0.7Y0.1Yb0.1O3-delta interface, thus increasing the joint strength from-25.3 to-32.4 MPa. Obtained joints maintain long-term stability in oxidizing and reducing atmospheres at 600 & DEG;C, suggesting the applicability of Y2W3O12@SiO2 composite particles in fabricating PCFC stacks. Our work provides a new strategy for preparing NTE materials with controllable interfacial reactions and service capability under extreme conditions.

A Novel Ag Based Sealant for Solid Oxide Cells with a Fully Tunable Thermal Expansion

Enhancing the Long-Term Stability of Ag Based Seals for Solid Oxide Fuel/electrolysis Applications by Simple Interconnect Aluminization

Effective Ag–CuO Sealant for Planar Solid Oxide Fuel Cells

Investigation on Silver Electric Adhesive Doped with Al2o3 Ceramic Particles for Sealing Planar Solid Oxide Fuel Cell

Evaluation and Application of a Novel BaO–CaO–SiO2–CoO–B2O3 Based Glass-Ceramic Sealing Material for Solid Oxide Fuel Cells

Joining of Solid Oxide Fuel/electrolysis Cells at Low Temperature: A Novel Method to Obtain High Strength Seals Already at 300 °C

Optimization of Al2O3-glass composite seals for planar intermediate-temperature solid oxide fuel cells

Reactive Air Brazing of the YSZ/AISI 310s Couples Using a Novel Ag–Nb2O5 Sealant

Novel Al2O3-based Compressive Seals for IT-SOFC Applications

Silver Particle Interlayer with High Dislocation Density for Improving the Joining of BaZr0.1Ce0.7Y0.1Yb0.1O3-δ Electrolyte and AISI 441 Interconnect

Development of Al2o3/Glass-Based Multi-Layer Composite Seals for Planar Intermediate-Temperature Solid Oxide Fuel Cells

Compatibility Between Glass Sealants and Electrode Materials of Solid Oxide Fuel Cells

Fabrication of 3D Ni Nanosheet Array on Crofer22APU Interconnect and NiO-YSZ Anode Support to Sinter with Small-Size Ag Nanoparticles for Low-Temperature Sealing SOFCs

Y2W3O12@SiO2 Composite Particles for Regulating Thermal Expansion and Interfacial Reactions in BaZr0.1Ce0.7Y0.1Yb0.1O3-δ/AISI 441 Joints

Analysis on Compatibility between Glass-Ceramic Sealants and the Components of Solid Oxide Fuel Cells

Study on expansion characteristics of Al–Al2O3 composite seals for intermediate‐temperature solid oxide fuel cell

The effect of CaO/MgO content on properties of barium aluminosilicate sealants for solid oxide fuel cells

A Novel Ag–CuAlO2 Sealant for Reactive Air Brazing of 3YSZ and AISI 310S

Calcium–Borosilicate Glass-Ceramics as a Sealant for Solid Oxide Fuel Cells

Thermal cycle stability of Al2O3-based compressive seals for planar intermediate temperature solid oxide fuel cells

Performance of Al2O3 Particle Reinforced Glass-Based Seals in Planar Solid Oxide Fuel Cells