Abstract:To investigate the carbonation regularity in concrete of 100mm×100mm×400mm, in the environment, (20±3)% (volume fraction) concentration of CO2, (70±5)% relative humidity and (20±2)°C temperature. The concrete specimens were divide into two parts: curing 28dayswith temperature of (20±2)°C and the relative humidity ⩾95% (named wet curing), and then curing for 3years (named A condition) with the relative humidity of (60±5)% and the temperature of (20±2)°C (named dried curing) and long-age wet curing for 90days (named B condition). The water-binder ratio was 0.37, 0.45 and 0.53, the content of fly ash substituting for the equal quality of cement by mass was 0%, 30% and 60%, respectively. Based on the scanning electron microscope (SEM) morphology of the interfacial transition zone of concrete’s coarse aggregate and X-ray diffraction (XRD) analysis, the influence mechanism of wet curing for 90days on the fly ash concrete carbonation resistance ability was analyzed. The results show that the wet curing for 90days had the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption on the concrete carbonation resistance ability. In the case of high fly ash content with low water-binder ratio or low fly ash content with high water-binder ratio, the dense effect of the interfacial transition zone of concrete’s coarse aggregate occupied a dominant position, and the carbonation resistance ability was greatly improved after wet curing for 90days. The average increment value of carbonation depth of fly ash concrete in each group decreased by 53.5% compared with the specimens cured under A condition. When the water-binder ratio and the fly ash content were either higher or lower, the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption had little significant effect on the concrete carbonation resistance ability, and the wet curing for 90days had no obvious influence on improving the carbonation resistance ability. At present, the average increment value of carbonation depth of fly ash concrete in each group decreased only by 11.5% of that under A condition.

Carbonation Performance of Concrete with Fly Ash As Fine Aggregate after Stress Damage and High Temperature Exposure

Carbonation Curing of Industrial Solid Waste‐based Aerated Concretes

Steel Corrosion and Corrosion-Induced Cracking in Reinforced Concrete with Carbonated Recycled Aggregate

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Effects of Micro-Environmental Climate on the Carbonation Depth and the Ph Value in Fly Ash Concrete

Effect of decarbonization of high carbon fly ash on workability, mechanical properties and durability of concrete

STUDY ON CARBONATION OF FLY ASH CONCRETE WITH FREEZE-THAW CYCLE

Durability of High-Volume Fly Ash Concrete Subjected to Drying-Wetting Cycles and Carbonation Coupling Effects

Multi-dimensional carbonation and service life prediction model of fly ash concrete subjected to flexural stress and CO2 attack

Long-Age Wet Curing Effect on Performance of Carbonation Resistance of Fly Ash Concrete

1D and 2D carbonation of fly ash concrete under flexural stress

The Effect of the Material Factors on the Concrete Resistance Against Carbonation

Experimental research on combined action of freeze-thaw cycles and carbonation for concrete structures

Evaluations of frost and scaling resistance of fly ash concrete in terms of changes in water absorption and pore structure under the accelerated carbonation conditions

Effect of Carbonation Curing on Durability of Cement Mortar Incorporating Carbonated Fly Ash Subjected to Freeze-Thaw and Sulfate Attack

Carbonation Characteristics of Concrete with Different Fly–Ash Contents

STRESS-CARBONATION OF FLY ASH CONCRETE

Chloride penetration in concrete exposed to cyclic drying-wetting and carbonation

EXPERIMENTAL STUDY ON CARBONATION PROPERTIES OF CONCRETE BASED ON BENDING LOAD DAMAGE

Investigation on Durability of Fly Ash Aerated Concrete

2D and 3D carbonation of fly ash concrete