Abstract:Herein, ordinary silicate concrete specimens are prepared to study the damage law of a cement-concrete material under the effects of salt erosion and a freeze–thaw environment. NaCl, NaHCO3, and Na2SO4 solutions are separately produced, according to the characteristics of saline soil, to conduct an experimental study on the concrete characteristics during quick salt freezing cycles, and to analyse the changes in its compressive strength, mass loss, and dynamic elastic modulus (DEM) under freeze–thaw cycles. Low-field nuclear magnetic resonance (NMR) and scanning electronic microscopy are used to investigate the change in the microstructure of concrete specimens under salt freeze–thaw cycles (FTCs). The results show the loss in compressive strength, mass, DEM, and NMR spectrum signal increased by 1.5–3 times, 3–5 times, 1.5–2.5 times, and 2–4 times, respectively, for concrete specimens under 50–100 FTCs in 6.8% composite salt solution, in comparison to fresh water. Apparent spalling, decreases in the DEM, and reductions in the compressive strength occur in concrete when increasing the number of salt FTCs. The number of internal cracks in the concrete structure increase under the combined action of salt crystallization, moisture absorption, and freeze–thaw. The changes in the internal microscopic pore volume in concrete structures exhibit the same trend with changes in the macro mechanical properties of concrete. The correlation coefficients between the changes in each peak in the NUR spectrum and the changes in the compressive strength of concrete specimens under FTCs in freshwater or low-concentration salt solutions are both larger than 0.7, calculated using the grey correlation degree method. Therefore, these changes could be used as a potential evaluation index for salt frozen damage to concrete structures.

Experimental research on combined action of freeze-thaw cycles and carbonation for concrete structures

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

STUDY ON CARBONATION OF FLY ASH CONCRETE WITH FREEZE-THAW CYCLE

Tests for properties of concrete under alternate freeze-thaw and carbonation actions

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Two‐dimensional Rigid Body Spring Method Based Micro‐mesoscale Study of Mechanical Strengthening/damaging Effects to Concrete by Frost Action

Experimental Study of Mechanical Properties of Concrete after Freeze-Thaw Exposures

Experimental Study on Mechanical Properties and Pore Structure Deterioration of Concrete under Freeze–Thaw Cycles

Effect of Carbonation Curing on Durability of Cement Mortar Incorporating Carbonated Fly Ash Subjected to Freeze-Thaw and Sulfate Attack

Experimental Research on Chloride Ingress into Concrete Exposed to Freeze-Thaw Cycles

Chloride Penetration and Pore Structure of Air Entrained Concrete Subjected to Freeze-Thaw Cycles

Evaluations of frost and scaling resistance of fly ash concrete in terms of changes in water absorption and pore structure under the accelerated carbonation conditions

Experimental Evaluation of the Concrete Damage and Pore Characteristics under Salt-Freezing Cycles

2D and 3D carbonation of fly ash concrete

Concrete Carbonation of Deep Burial Storage Constructions under Model Aging Conditions

Experiment and research of prestressed concrete structure in carbonation corrosive environments

Research progress of the thermophysical and mechanical properties of concrete subjected to freeze-thaw cycles

Experimental studies on mechanical properties of concrete under freeze-thaw action

FRACTURE TOUGHNESS AND FRATURE ENERGY OF CONCRETE SUBJECTED TO FREEZE-THAW CYCLES

Experimental Study on Freezing and Thawing Cycles of Shrinkage-Compensating Concrete with Double Expansive Agents

Mechanism of Concrete Damage under the Coupled Action of Freeze-Thaw Cycle and Low-Stress Impact Fatigue Load：from Pore Structure to Energy Dissipation