Abstract:To investigate the carbonation regularity in concrete of 100mm×100mm×400mm, in the environment, (20±3)% (volume fraction) concentration of CO2, (70±5)% relative humidity and (20±2)°C temperature. The concrete specimens were divide into two parts: curing 28dayswith temperature of (20±2)°C and the relative humidity ⩾95% (named wet curing), and then curing for 3years (named A condition) with the relative humidity of (60±5)% and the temperature of (20±2)°C (named dried curing) and long-age wet curing for 90days (named B condition). The water-binder ratio was 0.37, 0.45 and 0.53, the content of fly ash substituting for the equal quality of cement by mass was 0%, 30% and 60%, respectively. Based on the scanning electron microscope (SEM) morphology of the interfacial transition zone of concrete’s coarse aggregate and X-ray diffraction (XRD) analysis, the influence mechanism of wet curing for 90days on the fly ash concrete carbonation resistance ability was analyzed. The results show that the wet curing for 90days had the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption on the concrete carbonation resistance ability. In the case of high fly ash content with low water-binder ratio or low fly ash content with high water-binder ratio, the dense effect of the interfacial transition zone of concrete’s coarse aggregate occupied a dominant position, and the carbonation resistance ability was greatly improved after wet curing for 90days. The average increment value of carbonation depth of fly ash concrete in each group decreased by 53.5% compared with the specimens cured under A condition. When the water-binder ratio and the fly ash content were either higher or lower, the positive effect of dense interfacial zone and the negative effect of calcium hydroxide consumption had little significant effect on the concrete carbonation resistance ability, and the wet curing for 90days had no obvious influence on improving the carbonation resistance ability. At present, the average increment value of carbonation depth of fly ash concrete in each group decreased only by 11.5% of that under A condition.

STUDY ON CARBONATION OF FLY ASH CONCRETE WITH FREEZE-THAW CYCLE

Development of Internal Moisture Transfer and Cumulative Residual Strain in Concrete under Freeze-Thaw Cycles

Tests for properties of concrete under alternate freeze-thaw and carbonation actions

RESEARCH ON 2-DIMENSION,3-DIMENSION CARBONATIONS AND SUPERPOSITION COEFFICIENT OF FLYASH CONCRETE

Effect of decarbonization of high carbon fly ash on workability, mechanical properties and durability of concrete

Experimental investigation on anti-freeze behavior of plain concrete

Experimental research on combined action of freeze-thaw cycles and carbonation for concrete structures

2D and 3D carbonation of fly ash concrete

EXPERIMENTAL STUDY OF PERFORMANCE OF FLY ASH FIBER CONCRETE UNDER THE ACTION OF SALT FROST

1D and 2D carbonation of fly ash concrete under flexural stress

Multi-dimensional carbonation and service life prediction model of fly ash concrete subjected to flexural stress and CO2 attack

Influence of Fly Ash on Concrete Permeability under Freezing-Thawing Cycle Condition

Long-Age Wet Curing Effect on Performance of Carbonation Resistance of Fly Ash Concrete

Investigation on Durability of Fly Ash Aerated Concrete

STRESS-CARBONATION OF FLY ASH CONCRETE

Effect of Carbonation Curing on Durability of Cement Mortar Incorporating Carbonated Fly Ash Subjected to Freeze-Thaw and Sulfate Attack

Carbonation Characteristics of Concrete with Different Fly–Ash Contents

Experimental investigation on anti-freeze behavior of confined concrete

Evaluations of frost and scaling resistance of fly ash concrete in terms of changes in water absorption and pore structure under the accelerated carbonation conditions

Durability of High-Volume Fly Ash Concrete Subjected to Drying-Wetting Cycles and Carbonation Coupling Effects

Carbonation Depth Prediction of Fly Ash Concrete Subjected to 2-and 3-Dimensional CO 2 Attack