Abstract:Text Mn/CeO2 catalysts modified by doping of Ti or Sn were investigated for low temperature selective catalytic reduction (SCR) of NO by NH3 with the aim of studying the effects of Ti, Sn doping on the catalytic performance. Ceria-based solid solutions (Ce0.8Ti0.2O2 and Ce0.8Sn0.2O2) were synthesized via inverse co-precipitation, and used as supports to prepare MnOx/Ce0.8M0.2O2 (M =Ti4+, Sn4+) catalysts through wetness impregnation method. The results showed that doping of Ti or Sn to the CeO2 support increase the NO removal efficiency. A NO conversion of more than 90 % was obtained over the Mn/CeTi catalyst at the temperature window of 175 ∼ 300 ◦C under a gas hourly space velocity (GHSV) of 60,000 mL•g–1•h–1. Catalysts modified by Ti and Sn were also found to obtain higher SO2 resistance than Mn/CeO2 catalyst. More than 90% NO conversion and 95% N2 selectivity could be provided by Mn/CeTi catalyst in the presence of 100 ppm SO2 at 250 ◦C for 10 h. A series of characterization techniques, namely XRD, BET, H2-TPR, XPS, NH3-TPD and in situ DRIFTS were used to elucidate the structure and surface properties of the obtained supports and catalysts. The results indicate that doping of Ti or Sn brings about catalysts with favorable properties such as higher BET surface area, better oxygen storage capacity and stronger surface acidity. The relative amount of Mn4+, Ce3+, adsorbed oxygen species and oxygen vacancies on the surface of catalysts are in the order of Mn/CeTi[U+FF1E]Mn/CeSn[U+FF1E]Mn/CeO2, which is thought to make positive a contribution to the low-temperature SCR activity. The promoted SCR activity is considered as well to be related to the dual redox cycles in Mn/CeTi (Mn4+ + Ce3+ leftrightarrow Mn3+ + Ce4+, Ce4+ + Ti3+ leftrightarrow Ce3+ + Ti4+) and Mn/CeSn (Mn4+ + Ce3+ leftrightarrow Mn3+ + Ce4+, Ce4+ + Sn2+ leftrightarrow Ce3+ + Sn4+ ) catalysts.

Effect of Ceria Doping on Catalytic Activity and SO2 Resistance of MnOx /tio2 Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Investigation on the redox/acidic features of bimetallic MOF-derived CeMOx catalysts for low-temperature NH3-SCR of NOx

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Effect of ceria doping on SO2 resistance of Mn/TiO2 for selective catalytic reduction of NO with NH3 at low temperature

Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low-temperature

Effect of Metal Ions Doping (M = Ti4+, Sn4+) on the Catalytic Performance of MnOx/CeO2 Catalyst for Low Temperature Selective Catalytic Reduction of NO with NH3

Ti or Sn Doping As a Way to Increase Activity and Sulfur Tolerance of Mn/CeO2 Catalyst for Low Temperature NH3 Selective Catalytic Reduction of NO

Effect of the Addition of Ce to MnOx/Ti Catalyst on Reduction of N2O in Low‐temperature SCR

The role of cerium in the improved SO2 tolerance for NO reduction with NH3 over Mn-Ce/TiO2 catalyst at low temperature

CeO 2 Catalysts for NH 3 ‐ SCR at Low Temperatures

Low-temperature Selective Catalytic Reduction of NO with NH3 over MnCe Oxides Supported on TiO2 and Al2O3: A Comparative Study

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

Low-temperature selective catalytic reduction of NO with NH3 over Mn–Ce–Ox/TiO2: a comparison between catalyst preparation methods

Performance of Low-temperature SCR of NO with NH3 over MnOx/Ti-based catalysts

Comparison of low-temperature catalytic activity and H2O/SO2 resistance of the Ce-Mn/TiO2 NH3-SCR catalysts prepared by the reverse co-precipitation, co-precipitation and impregnation method

Improvement of Activity and SO2 Tolerance of Sn-Modified MnOx–CeO2 Catalysts for NH3-SCR at Low Temperatures

In situ IR studies of Co and Ce doped Mn/TiO 2 catalyst for low-temperature selective catalytic reduction of NO with NH 3

CeO2 Nanoparticle-Loaded MnO2 Nanoflowers for Selective Catalytic Reduction of NOx with NH3 at Low Temperatures

Promotion Effect and SO2 Tolerance of Sb-Modified Ce-Co/TiO2 Catalyst for Low-Temperature Selective Catalytic Reduction of NOx with NH3

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR