Abstract:ABSTRACT Internal corrosion is a problem for steel pipelines transporting natural gas or CO2 containing water and partial pressures of H2S higher than 0.3 kPa (0.05 psi). This work aims to mitigate internal corrosion in steel pipelines transporting natural gas containing H2S using cold spray coatings. Two types of the cold spray binary metallic coatings (zinc chromium (ZnCr), zinc niobium (ZnNb)) were studied using electrochemical techniques: potentiodynamic polarization (PDP), linear polarization resistance (LPR), and electrochemical impedance spectroscopy (EIS). The corrosion resistance of cold spray coatings (ZnCr, ZnNb) was evaluated in an environment containing 4 bar CO2 pressure, simulating the partial pressures found in gas transmission lines over a solution of 3.5 wt.% NaCl heated to 40 °C. A concentration of 0.003 M Na2S2O3.5H2O, which corresponds to H2S partial pressures around 0.079 bar (1.146 psi), was used to simulate sour conditions. Post-corrosion surface characterization was performed using a scanning electron microscope (SEM) equipped with energy dispersive X-ray spectroscope (EDS) and X-ray diffraction analysis (XRD). The data showed that the presence of 0.003 M Na2S2O3.5H2O shifted the corrosion potential to more anodic values and decreased the corrosion current density. Both coatings showed similar behavior after 1 hour of exposure in the CO2/H2S environment, indicating that similar electrochemical reactions were occurring on ZnNb and ZnCr. SEM images and EDS surface analyses for specimens showed a significant change in the surface chemical composition of carbon steel coated with ZnNb and ZnCr after 24 hours of immersion. In the presence of thiosulfate (under sour conditions), the formation of corrosion product layers (ZnCO3 and ZnS) on top of ZnNb and ZnCr coatings increased their corrosion resistance, which helped to reduce their corrosion by a factor of 2. Under a sweet environment. The corrosion rates for steel coated with cold spray coatings after 14 days of exposure are lower than that for galvanized steel by a factor of 5 due to the ZnCO3 layer formed on top of the coatings. The ZnCO3 layer formed on the steel surface acts as a physical barrier against corrosion by blocking the diffusion of corrosive species to the surface. No localized attack was observed. ZnCr Cold spray coating with defect showed promising corrosion protection against CO2 corrosion (sweet corrosion) after 14 days of exposure to a CO2 environment. The scratch on the coating simulated damage created in service, and it was deep enough to expose the substrate material (steel). The formation of zinc oxide (ZnO) and zinc carbonate (ZnCO3) on the scratch confirmed the cathodic protection of the steel by ZnCr and ZnNb coatings.

Corrosion Performance of Nanocomposite Coatings in Moist SO2 Environment

Corrosion Behavior of Ni-P-Nano-Al2o3 Composite Coating in the Presence of Anionic and Cationic Surfactants

Characterization and corrosion behavior of electroless Ni-Mo-P/Ni-P composite coating in CO2/H2S/Cl− brine: Effects of Mo addition and heat treatment

Insights into the Electrochemical Corrosion Behavior and Mechanism of Electroless Ni-P Coating in the CO2/H2S/Cl− Environment

Studies on nano-hybrid biopolymer composite coating on corroded steel to improve the corrosion resistance and hydrophobicity of the surface

Evaluation of Corrosion Behaviour of Ni/Wc-Mos2 Composite Coatings Prepared by Jet Electrodeposition with Different Mos2 Doping Concentrations

Study on the Corrosion Resistance of Superhydrophobic Ni-Co- P-BN(h) Nanocomposite Coatings Prepared by Electrochemical Machining and Fluorosilane Modification

Corrosion Resistance and Micro-Tribological Properties of Nickel Hydroxide-Graphene Oxide Composite Coating

Electrodeposition fabrication of corrosion−resistant Ni–based composite film on surface of Cu: Role of conductive YSZ and non−conductive Si 3 N 4 nanoparticles

Corrosion Behavior of Al2O3-40TiO2 Coating Deposited on 20MnNiMo Steel via Atmospheric Plasma Spraying in Hydrogen Sulfide Seawater Stress Environments

Sonication assisted superior anti-corrosion properties of cathodically deposited novel nickel-graphene oxide-zinc oxide coating

Graphene-Reinforced Zn-Ni Alloy Composite Coating on Iron Substrates by Pulsed Reverse Electrodeposition and Its High Corrosion Resistance

Nanocomposite coatings based on graphene and siloxane polymers deposited by atmospheric pressure plasma. Application to corrosion protection of steel

Electrochemical Properties and XPS Analysis of Ni-B/SiC Nanocomposite Coatings

Mechanical and Corrosion Resistance Properties of Tio2 Nanoparticles Reinforced Ni Coating by Electrodeposition

Hybrid Zinc Coatings with Chitosan/Alginate Encapsulated CuO-Nanoparticles for Anticorrosion and Antifouling Protection of Mild Steel

Fabrication of Pb-Co-ZrO 2 nanocomposite coatings and correlation of corrosion mechanisms with electronic work functions

Corrosion of Zinc Cold Spray Coatings in a Wet Sweet and Sour Gas Environment.

Investigation on corrosion resistance of electroless Ni-W-P coatings co-deposited with SiO2 nanoparticles

Corrosion behaviour of iron and nickel aluminide coatings under the synergistic effect of NaCl and water vapour

Investigating the Microstructure and Anti-corrosion Behavior of the Electroless Ni-P-Y2O3 Composite Coatings