Microstructure Evolution and Superelasticity of Ti-24Nb-xZr Alloys Fabricated by Spark Plasma Sintering

H. Z. Lu,C. Yang,X. X. Li,Q. R. Cheng,H. W. Ma,Z. Wang,X. Q. Li,S. G. Qu

DOI: https://doi.org/10.1016/j.jallcom.2020.153875

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:This study presents the effects of Zr addition on microstructure, phase composition, and superelasticity of Ti-24Nb-xZr (at.%, x = 0, 2, 6) alloys fabricated by spark plasma sintering (SPS). The obtained microstructures were studied using X-ray diffraction and electron microscopy, and the mechanical properties and shape memory properties were evaluated through both compressive testing and cyclic compression experiments. The results show the addition of Zr is beneficial to the formation of the alpha '' phase and beta-Ti grain refinement. The sintered Ti-24Nb-6Zr shows better compressive yield strength (1457 MPa), ultimate strength (2458 MPa), and strain (45.31%). Cycle compression tests reveals that the Ti-24Nb-6Zr alloy demonstrates stable recoverable strain of 4.11% and remarkable recovery strain rate of 98.1% in the second cycle, and a maximum 7.8% recovery strain and good recovery strain rate of 82.4% in the fifth cycle. In contrast, the sintered Ti-24Nb alloy exhibits recoverable strain of 4.58%, a recovery strain rate of 96.6% in the third cycle, and only 48.8% recovery strain rate in the fifth cycle. The transmission electron microscopy results indicate that the formation of microcracks and dislocations during the cycle compression results in significant recovery strain reduction for the Ti-24Nb alloy. The results provide guidelines to design high-performance Ti-24Nb-based alloys with excellent shape memory properties for structural applications. (C) 2020 Elsevier B.V. All rights reserved.