Interface Improvement of Li 6.4 La 3 Zr 1.6 Ta 0.6 O 12 @La 2 Sn 2 O 7 and Cathode Transfer Printing Technology with Splendid Electrochemical Performance for Solid-State Lithium Batteries
Huirong Liu,Jianling Li,Wei Feng,Feiyu Kang
DOI: https://doi.org/10.1021/acsami.1c09692
2021-08-12
Abstract:All-solid-state lithium batteries (ASSLBs) are regarded as the next-generation energy storage devices due to their superior safety and potential high energy density. In ASSLBs, a composite solid electrolyte is the most competitive candidate. The interface between the cathode and composite electrolyte and the interface between ceramic and polymers are important factors affecting the performance of solid-state batteries. The interface between the superionic conductor and polymer electrolyte (polyvinylidene fluoride) was modified by in situ synthesis of a pyrochlore-type La2Sn2O7 (LSO) ceramic layer on the surface of Li6.4La3Zr1.4Ta0.6O12 (LLZTO). The synthesis of LSO consumes La in LLZTO, increases the concentration of lithium ions in LLZTO, and significantly improves the conductivity of the composite electrolyte (). Compared with the pristine sample (3.15 × 10–5 S cm–1), the conductivity of %LSO-CSE was improved by an order of magnitude (as high as 1.30 × 10–4 S cm–1). At the same time, the lithium-ion transference number of %LSO-CSE and %LSO-CSE was 0.42 and 0.44, respectively (%LSO-CSE was 0.36). Meanwhile, the pyrochlore structure of LSO has the characteristics of fast energy storage and conversion, so the full cell LiFePO4||Li showed superior rate capability and cycling stability. As anticipated, the discharge capacities of LiFePO4|%LSO-CSE|Li were 141.4 mA h g–1 (1 C) and 128.1 mA h g–1 (2 C), respectively. However, the discharge capacities of pristine batteries without LLZTO modification were 122.5 mA h g–1 (1 C) and 88.7 mA h g–1 (2 C). After 400 cycles, the discharge capacity of the LiFePO4|%LSO-CSE|Li remained at 110.6 mA h g–1, the Coulomb efficiency was 99.4%, and the capacity retention rate was 72% compared to 75.5 mA h g–1, 98, and 49% for the pristine one, respectively. In addition, the transfer printing (TP) technology was used to improve the interface between the cathode and the solid-state electrolyte, which immensely increased the energy density (without aluminum foil). Compared with the original interface impedance of 379 Ω, the interface impedance was significantly reduced to 213 Ω. This uniquely developed combined with the TP technology can provide an effective approach for the development of all-solid-state batteries.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c09692.SEM images and EDS maps of ; particle size distribution of LLZTO; optical photographs of the tensile test of the composite electrolyte membrane; electronic conductivity of ; and galvanostatic cycles of Li|%LSO-CSE|Li (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology