Abstract:Low alloy SA508 bainitic steel is often welded to 300 series austenitic stainless steel in nuclear power plants. These dissimilar metal weldments use 309L butter applied to the low alloy steel and 308L groove filler material to join the 309L to austenite. High alloy steels (such as the 308L and 309L material used here) have been identified as having greater susceptibility to irradiation-assisted stress corrosion cracking (IASCC). Evidence is presented here of cracking under tensile loads in 309L weldment butter in LWR hydrothermal conditions that correlates irradiation induced changes at δ ferrite−γ austenite phase boundaries and γ−γ grain boundaries; specifically intergranular Cr 23 C 6 precipitates. Cracking is not observed in irradiated 308L groove filler under the same conditions. Both the 309L butter and 308L filler material have a duplex or mixed δ−γ phase microstructure due to solidification during the welding procedure. We have performed constant extension rate autoclave immersion tests in BWR normal water chemistry hot water (288 °C, 10 MPa, 2000 wt. ppb dissolved oxygen, <100 nS/cm conductivity, neutral pH) of proton irradiated (2 MeV, approximately 3 displacements per atom at a depth of 10 μm). Proton irradiation to the dpa levels used here induced Cr 23 C 6 carbide precipitation at γ−γ grain boundaries and δ−γ phase boundaries in the 309L butter but not the 308L filler. Cracking was observed in the proton-irradiated volume of 309L at these interfaces in the vicinity of the Cr 23 C 6 precipitates. We hypothesis the SA508 is the source of carbon in the 309L butter. Cr depletion at γ−γ grain boundaries was also observed and may also be a root cause of cracking. The 309L butter is under significant tensile residual stress in the weldment that adds to applied tensile loads and this too may be a contributing factor.

Stress Corrosion Cracking of the Fusion Boundary for 304L/82 Dissimilar Metal Weld Joint in Simulated Primary Water

Microstructure, Hardness, and Residual Stress of the Dissimilar Metal Weldments of SA508-309L/308L-304L

Environmentally assisted cracking in the fusion boundary region of a SA508-Alloy 52M dissimilar weld joint in simulated primary pressurized water reactor environments

Correlating oxidation resistance to stress corrosion cracking of 309L and 308L stainless steel claddings in simulated PWR primary water

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Chloride-Induced Stress Corrosion Cracking of Friction Stir-Welded 304L Stainless Steel: Effect of Microstructure and Temperature

Effect of Fusion Boundary Microstructure on Flow-Accelerated Corrosion Cracking

Effect of Mechanical Heterogeneity on Strain and Stress Fields at Crack Tips of SCC in Dissimilar Metal Welded Joints

Stress Corrosion Cracking of E690 Steel As a Welded Joint in a Simulated Marine Atmosphere Containing Sulphur Dioxide

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

Sulphide Stress Cracking Behaviour of the Dissimilar Metal Welded Joint of X60 Pipeline Steel and Inconel 625 Alloy

Effect of material chemical composition on oxidation and stress corrosion cracking of the submerged arc welding Alloy 52M overlay in a simulated PWR primary water

Investigation of Multi-Factor Stress Corrosion Cracking Failure of Safe-End Feedwater Lines of Submarine Power System

Effect of inhomogeneous microstructure on the stress corrosion cracking behavior of 316LN stainless steel weld joint under high-temperature and high-pressure water small punch test

Study on Corrosion Fatigue Behavior of 304L Austenite Stainless Steel in 325 °C High-Temperature Water Environment

Insights into the role of partially mixed zones in sulfide stress corrosion cracking of the inconel 625/X80 weld overlay

Environment assisted cracking of 308L weld metal in high temperature water

Effect of ferrite and grain boundary characteristics on corrosion properties of thermal simulated 316 L heat affected zone

Fractography of Stress Corrosion Cracking of 20% Cold Worked Type 304 H Stainless Steel Containing δ-Ferrite in Oxidizing Primary Water

Effects of Welding and Constraint Conditions on the Welding Residual Stress and Hardness of Type 316 Stainless Steel Pipe

Effect of Inhomogeneous Mechanical Properties on the Stress-Strain Field at the Crack Tip and Crack Growth Direction in Dissimilar Metal Welded Joints