Abstract:This research aims to study the microstructure characteristics, mechanical properties, and corrosion behaviors of the dissimilar autogenous laser beam welded joint of pipeline steel (X-70) and super duplex stainless steel (sDSS 2507). Pipelines for the transmission of oil and gas and risers for offshore oil and gas drilling require this dissimilar joint. A dissimilar joint must maintain its properties and be defect-free under such challenging operating conditions. The microstructure of the interface, weld zone and heat-affected zone (HAZ) were all investigated thoroughly using optical microscopy (OM) and scanning electron microscopy (SEM) equipped with energy-dispersive spectroscopy (EDS). This dissimilar joint had significant microstructure anomalies in the weld and interfaces. Microstructure inhomogeneity's effect on welded joint mechanical properties, including microhardness, tensile and impact strength, was also studied. The linear potentiodynamic polarisation test in neutral 3.5 wt.% NaCl solution was used to study this weldment's corrosion behavior. The corroded surfaces were examined using an OM and SEM for the surface morphology investigation of corroded specimens. The macro-optical investigation has revealed full penetrations in the weld without any inclusions or porosities. The interface between the sDSS 2507 weld zone and the X-70 coarse grain heat-affected zone (CGHAZ) indicated a peak hardness of 418 Hv 0.5 . With an average of 345 Hv 0.5 , the WZ's hardness variation was reported to be in the 298–420 Hv 0.5 range. The hardness of the X-70/sDSS 2507 weld interface was assessed to be greater than that of the other region of weldments. An untempered martensitic region in WM and the CGHAZ of X-70, and the presence of M-A components are credited with the increase in hardness. The welded joint achieved reasonably excellent strength and ductility and met the marine and offshore standards requirements. The base metals and weldment for X-70 and sDSS 2507 have respective ultimate tensile strengths (UTS) of 610 ± 6 MPa, 995 ± 8 MPa, and 675 ± 10 MPa. The tensile findings revealed that the fracture location for weldment was evident in the X-70 base metal, ensuring that the weld metal was of adequate strength for the laser-weld joints. It was observed that the weldment's WM had the lowest impact strength. The Charpy impact toughness of the weld metal, however, was higher than both the ASME standard (> 41 J) and the EN 1599:1997 standards (> 47 J). The sDSS 2507 BM (310 ± 4 J) clearly outperforms the weld zones (185 ± 3 J) and X-70 base metal (295 ± 2 J) in terms of impact strength. The electrochemical corrosion test shows the corrosion potential, and the weld zone's corrosion rate is between sDSS 25,070 (− 260 ± 1.3 mV, 0187 ± 0.002 mm/year) and X-70 base metal (− 454 ± 1.8 mV, 0.321 ± 0.017 mm/year). Additionally, the surface morphologies and the electrochemical measurements matched significantly.

Sulphide Stress Cracking Behaviour of the Dissimilar Metal Welded Joint of X60 Pipeline Steel and Inconel 625 Alloy

H2S Stress Corrosion Tests of Welded Joint for X65 Pipeline Steel and Finite Element Numerical Analysis of Crack Tip

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment

Assessing the Residual Stresses in Dissimilar Welded Joint: Depth-Sensing Indentation Testing and Numerical Simulation

Insights into the role of partially mixed zones in sulfide stress corrosion cracking of the inconel 625/X80 weld overlay

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

Sulfide Corrosion Cracking of Linepipe for Sour Gas Service

Microstructure and sulfide stress corrosion cracking of the Inconel 625/X80 weld overlay fabricated by cold metal transfer process

Sulfide stress cracking (SSC) of a commercial Q345 pressure vessel steel in a wet H 2 S environment

Stress Corrosion Cracking of E690 Steel As a Welded Joint in a Simulated Marine Atmosphere Containing Sulphur Dioxide

Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials

Effect of Mechanical Heterogeneity on Strain and Stress Fields at Crack Tips of SCC in Dissimilar Metal Welded Joints

Stress corrosion cracking behavior of X80 pipeline steel under alternating current, Desulfovibrio desulfurican and cathodic protection potential

The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment

Identifying sulfide stress cracking stages on a HSLA pipeline steel in H2S environment by electrochemical noise

Investigation on the Fatigue Crack Propagation Behavior of L360MS Pipeline Steel Welded Joints with Inconel 625 Weld Metal

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Structure–property relationships and corrosion behavior of laser-welded X-70/UNS S32750 dissimilar joint

Corrosion performance of super duplex stainless steel and pipeline steel dissimilar welded joints: a comprehensive investigation for marine structures

Insight into the corrosion susceptibility and failure mechanism of Cu-Ni alloy pipeline welded joints in simulated marine environment

Studies on residual stresses and structural integrity of the dissimilar gas tungsten arc welded joint of sDSS 2507/Inconel 625 for marine application