Abstract:This work investigates the heterogeneous deformation and failure of HR3C austenitic stainless steel welded joints at room and typical service temperatures. Such types of welded joints are widely used in the new generation of fossil fuel power stations and are known to suffer from premature high temperature failure. Observation of in-service failures revealed that cracks may nucleate either in the heat affected zone or in the weld metal. The main objective of this work is to identify the local microstructural conditions and stress–strain fields responsible for both ductile failure and micro-crack nucleation within the weldment at low and high temperatures, respectively. To that purpose, a novel multi-scale micromechanics-based modelling framework is proposed. It relies on representative weld microstructure models digitally reconstructed from EBSD measurements, and dislocation density-based crystal plasticity models to describe the behaviour of individual grains in each weld region. A novel thermo-dynamically consistent relation for the configuration stored energy per unit volume is derived from the crystal plasticity framework. The single crystal models are calibrated and validated from a combination of uniaxial tensile tests on cross-weld specimens using high resolution digital image correlation techniques, representative volume elements of the polycrystals at the macro-scale, as well as micropillar compression tests at the scale of the individual grains. Predictions of heterogeneous inelastic deformation fields within the weldment at both 22 °C and 665 °C, and of micropillar compression behaviour of the individual weld single crystal phases are consistent with experimental data. The experimentally observed ductile failure of the weld metal at room temperature is successfully predicted using a Gurson-type void nucleation, growth and coalescence constitutive model. The suitability of the stored strain energy density and the accumulated plastic strain as crack initiation/creep failure indicators is investigated. It was found that predicted creep lifetimes with either indicator were very similar, and that they were relatively accurate for low stress levels.

Environmentally assisted cracking in the fusion boundary region of a SA508-Alloy 52M dissimilar weld joint in simulated primary pressurized water reactor environments

Effect of Fusion Boundary Microstructure on Flow-Accelerated Corrosion Cracking

Insights into the role of partially mixed zones in sulfide stress corrosion cracking of the inconel 625/X80 weld overlay

Microstructure, Hardness, and Residual Stress of the Dissimilar Metal Weldments of SA508-309L/308L-304L

Irradiation-assisted cracking of SA508-304L weldments with 308L groove filler and 309L butter in hot water immersion constant rate extension tests

Environment assisted cracking of 308L weld metal in high temperature water

Effect of Material Heterogeneity on Environmentally Assisted Cracking Growth Rate of Alloy 600 for Safe-End Welded Joints

Effect of material chemical composition on oxidation and stress corrosion cracking of the submerged arc welding Alloy 52M overlay in a simulated PWR primary water

Micro-mechanics investigation of heterogeneous deformation fields and crack initiation driven by the local stored energy density in austenitic stainless steel welded joints

In-situ SEM study of short fatigue crack propagation behavior in a dissimilar metal welded joint of nuclear power plant

Fracture Location Shift of Dissimilar Metal Welds under Coupled Thermal-Stress Effect

Effect of Inhomogeneous Mechanical Properties on the Stress-Strain Field at the Crack Tip and Crack Growth Direction in Dissimilar Metal Welded Joints

Analysis of Stress Corrosion Cracking Growth Rate in the Heat-Affected Zone of 316L Based on the Heterogeneity of the Mechanical Properties

Analysis of Crack Propagation Behaviors in RPV Dissimilar Metal Welded Joints Affected by Residual Stress

Experimental study on fatigue crack growth behavior and fracture toughness of SA508-III steel for nuclear reactor pressure vessel

Inhibiting weld cracking in high-strength aluminium alloys

Failure Analysis of Dissimilar Metal Welds between Ferritic Heat Resistant Steels and Austenitic Stainless Steels in Power Plant

Effect of Mechanical Heterogeneity on Strain and Stress Fields at Crack Tips of SCC in Dissimilar Metal Welded Joints

Welding hot cracking characteristics and fracture mechanisms of nickel‐based alloy NS1402 under different constraint conditions

Effect of thermal aging on the environmental assisted cracking behavior of 308L weld metal in high temperature water

Study on Stress Corrosion Cracking Behavior of Incoloy825/X65 Bimetallic Composite Pipe Welded Joint in Wet Hydrogen Sulfide Environment