Abstract:Fatigue crack initiation mechanism at high cycle regime in a bimodal Ti-5Al-7.5V alloy are investigated by fracture observations, focused-ion-beam cross-section and electron back-scattered diffraction characterizations. The aged Ti-5Al-7.5V exhibits superior tensile and fatigue properties, alongside a wide range of fatigue life when tested at the stress levels of - 700-800 MPa. Fatigue failure was dominated by surface and subsurface crack initiation at facets matching basal planes. These faceted primary alpha (alpha p) grains generally have a medium or high Schmid factor (SF) for basal < a > slip. Moreover, a basal faceting process also occurred in the "hard" grains, in which the c-axis of the HCP-alpha grains was approximately parallel to the loading axis so that the < a > type slips were thought to be suppressed. The observed internal microcracks were formed along the grain boundaries located in clusters of alpha p grains, especially along (0001) twist boundaries. Furthermore, transmission electron microscope observations evidenced the absence of intense slip bands within faceted grain and fatigued alpha p grains, which indicates that the facet growth should not along the pre-existing slip bands resulting from high cycle fatigue loadings. The pre-existing structural defects including dislocation networks and subgrain boundaries within alpha p grains are relatively stable configurations under fatigue loadings. The observed fine (-500 nm in diameter) silicides were widely dispersed, whether the silicide can act as the crack nucleation site still needs further more detailed studies and this remains an open question.

Faceted Crack Induced Failure Behavior and Micro-Crack Growth Based Strength Evaluation of Titanium Alloys under Very High Cycle Fatigue

Subsurface Facets-Induced Crack Nucleation Behavior and Microstructure-Based Strength Evaluation of Titanium Alloys in Ultra-Long Life Regime

Subsurface Facet-fisheye Induced Failure of Titanium Alloy under Very High Cycle Fatigue

Microstructure based cracking behavior and life assessment of titanium alloy under very-high-cycle fatigue with elevated temperatures

Fatigue Crack-Initiation Mechanisms of a Dual-Phase Titanium Alloy Exhibiting High Tensile and High-Cycle Fatigue Properties

Crack Initiation and Early Growth Behavior of TC4 Titanium Alloy under High Cycle Fatigue and Very High Cycle Fatigue

Subsurface Crack Nucleation and Growth Behavior and Energy-Based Life Prediction of a Titanium Alloy in High-Cycle and Very-High-cycle Regimes

Fatigue Crack Growth of TC17 Titanium Alloy with Three Microstructures

Fatigue cracking behavior and life assessment of TC11 titanium alloy in very high cycle regime at two working temperatures

Crack Initiation Mechanism in a High-Strength Ti-5Al-7.5V Alloy Subjected to High Cycle Fatigue Loading

Very High Cycle Fatigue of TC4 Titanium Alloy under Variable Stress Ratio: Failure Mechanism and Life Prediction

Microstructure-based Interior Cracking Behavior of Α + Β Titanium Alloy under Two Stress Ratios and Intermediate Temperature in the Very High-Cycle Fatigue Regime

Deformation in Fatigue Crack Tip Plastic Zone and Its Role in Crack Propagation of Titanium Alloy with Tri-Modal Microstructure

Cyclic Deformation and Microcrack Initiation During Stress Controlled High Cycle Fatigue of a Titanium Alloy

High-cycle Fatigue of a Titanium Alloy: the Role of Microstructure in Slip Irreversibility and Crack Initiation

Low-cycle Fatigue Behavior and Life Prediction of TA15 Titanium Alloy by Crystal Plasticity-Based Modelling

Microstructural Influences on the High Cycle Fatigue Life Dispersion and Damage Mechanism in a Metastable Β Titanium Alloy

Crystallographic Micro-Mechanism of Faceted Crack Initiation in Near-Α Titanium Alloy Ti6321 under Room-Temperature Fatigue and Dwell Fatigue Loadings

Investigation of Micro-Mechanisms for Facet Formation During Dwell Fatigue in Ti6321 Alloy with Equiaxed Microstructure

High Cycle and Very High Cycle Fatigue Properties and Microscopic Crack Growth Modeling of Ti‐6.5Al‐3.5Mo‐1.5Zr‐0.3Si Titanium Alloy at Elevated Temperatures

Quantitative Assessment of Microstructural Damage for Interior Crack Initiation and High Cycle Fatigue Life Modeling