Abstract:PtNi alloy nanoparticles supported on carbon (XC-72) are synthesized via a one-pot synthetic approach. This synthesized bimetallic composite offers several advantages, such as reduction of precious Pt along with an increase in activity due to the modified electronic structure. The prepared PtNi/C catalysts were employed as catalysts for NO removal both in a fixed-bed reactor and in a newly designed gas diffusion reactor. The performances of all prepared PtNi/C catalysts were higher than Pt/C at the same conditions and maintained a stable NO removal at a wide temperature window (100-300 degrees C), especially for Pt65Ni35 (more than 95% from 120 to 300 degrees C). This is attractive for low temperature SCR technology. According to XPS analysis, the surface layer phase was comprised of Pt contents with Ni being localized beneath the successive layers until Ni content increased to 67% mole ratio. The surface presence of Ni significantly affects the Pt electronic structure and raises the mass specific activity of Pt. Meanwhile, PtNi/C catalysts were introduced in a new gas diffusion reactor to remove NO under quantitatively less catalysts (30 mg), high NO concentration (1000 ppm), and at a high flow rate (resulting in a very short residence time of 0.09 s) condition. NO removal reaches almost 100% below 95 degrees C for all the PtNi catalysts and among all Pt65Ni35 exhibited the best performance. In addition, the influence of SO2 on the performance of Pt65Ni35 was also investigated, and the catalysts exposed a good antipoisonous property. The excellent performance of PtNi catalysts and a gas diffusion reactor are strongly recommended for their utilization as highly active and economical technology for NO removal.

In Situ Hydrogen Uptake and NOx Adsorption on Bifunctional Heterogeneous Pd/Mn/Ni for a Low Energy Path Toward Selective Catalytic Reduction

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Selective Catalytic Reduction of Nitric Oxide by Hydrogen over NiFe2−xPdxO4 Catalysts at Low Temperature

Selective catalytic reduction of nitrogen oxides by methane over Ni/H-USY catalysts

Pt-Doped NiFe2O4 Spinel As a Highly Efficient Catalyst for H2 Selective Catalytic Reduction of NO at Room Temperature

A stable Cu-polyatomic-cluster catalyst: Critical for methanol reforming deNOx at mild temperature

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Tunable Highly Dispersed Nia-xMnxAlOy Catalysts Derived from Layered Double Oxide for Low Temperature NOx Removal

Synergism Between Palladium and Nickel on Pd-Ni/TiO2 for H2-SCR: A Transient DRIFTS Study

Elucidating the Role of the State of Pd in the H 2 -SCR of NOx by Operando XANES and DRIFTS

Ni-Mn Bi-Metal Oxide Catalysts for the Low Temperature SCR Removal of NO with NH3

Fundamental investigation on layered double hydroxides derived mixed metal oxides for selective catalytic reduction of NOx by H2

Highly Selective Catalytic Reduction of No Via So2/H2o-Tolerant Spinel Catalysts at Low Temperature

Facile Synthesis of PtxNiy Catalyst Supported on Carbon for Low Temperature H2–SCR

Selective Catalytic Reduction of NO with NH3 over Mn–Fe/USY under Lean Burn Conditions

Novel Homogeneous and Mesoporous MnOx-Doped Ceria Nanosheets As Catalysts for Low-Temperature Selective Catalytic Reduction

Mechanism and Enhancement of the Low-Temperature Selective Catalytic Reduction of NOx with NH3 by Bifunctional Catalytic Mixtures

Selective catalytic reduction of NOx by H2 over a novel Pd/FeTi catalyst

110Th Anniversary: Recent Progress and Future Challenges in Selective Catalytic Reduction of NO by H2in the Presence of O2

Molecular-Level Insight into Selective Catalytic Reduction of NOx with NH3 to N2 over a Highly Efficient Bifunctional Va-MnOx Catalyst at Low Temperature

Metal-Organic Framework (Mof) Template Based Efficient Pt/Zro2@C Catalysts For Selective Catalytic Reduction Of H-2 Below 90 Degrees C