Abstract:In this study, a material with high photocatalytic activity was synthesized using ternary C/N/S-doped TiO2 nanorod array (TiO2); this was done using a practical and straightforward vapor-phase hydrothermal (VPH) method at a low temperature. The effect of C/N/S content on TiO2 morphology, optical, photocatalytic and photoelectrochemical (PCE) properties of the material was investigated by varying the quality of thiourea. C/N/S-TiO2 reduced the bonding rate of electron-hole pairs and enhances visible light absorption, photocatalytic, and PCE properties. The C/N/S doping could significantly adjust the absorption cut-off wavelengths (407-602 nm) and shorten the bandgap (3.04-2.18 eV) of TiO2. Under simulated sunlight, 8-C/N/S-TiO2 had the highest photocatalytic efficiency of 97.6% for methylene blue (MB) in 150 min with a rate constant of 0.0192min-1, which is approximately four times that of TiO2 (0.005 min-1). The 8-C/N/S-TiO2 photoelectrode had the lowest transfer resistance for interfacial charges and highest transient photocurrent of 33.5 μA/cm2, which is five times higher than that of TiO2 (6.6 μA/cm2). The 8-C/N/S-TiO2 exhibits the most extensive PCE behavior as a photoelectrode, and has a current density of 38.2 mA/cm2 at 2.5VRHE, which is about two times higher than TiO2 (19.1 mA/cm2). The favorable sunlight-driven photocatalytic activity is probably due to the synergistic effect of C/N/S-doping, which shifts the valence band maximum of TiO2 upward. This provides new ideas for future solar cells that can use dye-sensitized TiO2 nanorod arrays as photoanodes. It is noteworthy that VPH is a very effective strategy for fabricating semiconductors doped with multiple nonmetallic elements.A material with high photocatalytic activity was synthesized using ternary C/N/S-doped TiO2 nanorod array (TiO2); this was done using a practical and straightforward vapor-phase hydrothermal (VPH) method at a low temperature. The favorable sunlight-driven photocatalytic activity is probably due to the synergistic effect of C/N/S-doping, which shifts the valence band maximum of TiO2 upward. It is noteworthy that VPH is a very effective strategy for fabricating semiconductors doped with multiple nonmetallic elements.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21001441-fx1_lrg.jpg">Download : Download high-res image (84KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21001441-fx1.jpg">Download : Download full-size image</a></li></ol>

Low-temperature S-doping on N-doped TiO2 films and remarkable enhancement on visible-light performance

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Low Temperature Hydrothermal Synthesis of N-doped TiO2 Photocatalyst with High Visible-Light Activity

Enhancement of the Photocatalytic Activity of N-doped TiO2 Nanograss Array Films by Low-Temperature Sulfur Doping

N-doped TiO2 applied in low-temperature-based dye-sensitized solar cells

Simple fabrication and photocatalytic activity of S-doped TiO2 under low power LED visible light irradiation

Low temperature synthesis of visible light-driven vanadium doped titania photocatalyst

Fabrication of V-Doped TiO2 Nanoparticles and Photocatalytic Studies under Visible Light

Microstructures and Properties of N-Doped TiO_2 Films Grown by Dielectric Barrier Discharge Chemical Vapor Deposition

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Photonic, and Photocatalytic Behavior of Tio2 Mediated by Fe, Co, Ni, N Doping and Co-Doping

Microstructures and Properties of N-Doped TiO_2 Films Grown by Atmospheric Pressure Chemical Vapor Deposition

Enhancing Visible-Light Photocatalytic Activity of Α-Bi 2 O 3 Via Non-Metal N and S Doping

Low-temperature fabrication of brown TiO2 with enhanced photocatalytic activities under visible light

Low-temperature strategy for vapor phase hydrothermal synthesis of C\N\S-doped TiO2 nanorod arrays with enhanced photoelectrochemical and photocatalytic activity

Characterization and photocatalytic activity of Ni-doped tiO2 nano photocatalysts prepared by low temperature combustion synthesis]

Investigation of structure and properties of N-doped TiO2 thin films grown by APCVD

(Mo+n) Codoped TiO2 for Enhanced Visible-Light Photoactivity

Realizing high visible-light-induced carriers mobility in TiO 2-based photoanodes

Zinc-doping in TiO 2 films to enhance photovoltaic performance of Dye-sensitized solar cells

N-doping TiO2 thin film prepared by heat treatment in electric field