Abstract:The class of NbC-Ni cermets has emerged as a promising environmentally friendly alternative to WC-Co cemented carbide tools, although some inherent properties i.e. room temperature hardness and flexural strength, of NbC-Ni cermets may require further enhancements. To enhance the properties of NbC-Ni cermets, diverse methodologies were applied, including grain inhibition and the strengthening of the cermet through the use of reinforcements. This study systematically examined the impact of TiC additions, specifically at 10% and 20%, on both the microstructure and mechanical properties of NbC-12Ni-4VC-4Mo2C cermets. NbC-12Ni cermets were fabricated via vacuum liquid phase sintering (LPS) at 1400°C and 1450°C. Enhancements by incorporating 4% VC and 4% Mo2C, followed by TiC at 10% and 20% concentrations to the NbC-Ni-4VC4Mo2C cermet were made. XRD and SEM results confirm the formation of (Nb, X, Y) C solid solution cubic FCC carbides. Significant grain refinement was evident in the cermet samples, subjected to grain inhibition. The observed grain sizes ranged from a maximum of 6.84 μm (in NbC12Ni) to a minimum of 2.154 μm (in the sample containing 20% TiC) at 1450°C. The incorporation of 20TiC at 1450°C led to a remarkable 26.5% enhancement in average hardness compared to NbC-Ni cermet, and a 4.2% improvement over the 4VC4Mo2C cermet. At 1450°C, 20TiC reinforcement led to an average fracture toughness of 9.331 MPa√m, representing a 4.56% improvement over the 4VC4Mo2C cermet. However, there was a marginal reduction in toughness compared to the NbC-Ni cermet. Moreover, the addition of TiC led to a decrease in the flexural strength of the cermets, with a maximum flexural strength of 939 N/mm2 recorded for NbC-Ni-4VC4Mo2C, representing an 11.6% increase compared to the NbC-Ni cermet.

The investigation on the fabrication and microstructure of NbTi-(NbTi)C Fe-based composite

Effect of Nb addition on microstructure and mechanical properties of TiC/Ti-7.8Cr composites

Study on microstructure and bending properties of NbC/Fe cluster-reinforced steel-based laminated composite

Microstructures and mechanical properties of in-situ FeCrNiCu high entropy alloy matrix composites reinforced with NbC particles

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Thermal/kinetic study of the formation mechanism of NbC-Fe composite layer on the surface of GCr15 prepared by hot pressure diffusion

Microstructure and Mechanical Properties of Dual Scaled NbC/Ti2AlC Reinforced Titanium–Aluminum Composite

Effect of Nb addition on the microstructure and mechanical properties of additively manufactured Ti2AlC MAX-phase ceramic matrix composites

Microscopic and macroscopic interfacial studies of NbC reinforcement layer on GCr15 bearing steel surface prepared by in-situ reaction method

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

The microstructure of (Nb,Ti)C-35Ni(Y2O3) cermet

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effect of Nb content on mechanical reinforcement of the Cu-10Fe composites

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Microstructure and properties of Ti(C, N)-based cermet with multi-core-rim microstructure: effect of (Ti, W, Ta) (C, N) pre-solid solution composition

The microstructural evolution and enhanced mechanical properties of in-situ Ti(C, N)-reinforced CoCrFeNiTi high-entropy alloy composites fabricated via mechanical alloying and spark plasma sintering

In-situ synthesis of Al2O3-reinforced high Nb–TiAl laminated composite with an enhanced strength-toughness performance

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Synthesis and characterization of Mo@Ni core-shell composite powder-reinforced (W,Ti)C-based cermet

Experimental and thermodynamic investigation of gradient zone formation for Ti(C,N)-based cermets sintered in nitrogen atmosphere