Abstract:Crystalline ultra-high molecular weight polyethylene (UHMWPE) has the highest reported thermal conductivity at room temperature: 104 W/m·K, while theoretical predictions proposed an even higher value of 300 W/m·K. Defects and amorphous fraction in practical UHMWPE fibers significantly reduces the thermal conductivity from the ideal value. Although the amorphous effect can be readily analyzed based on the effective medium theory, the defect effects are poorly understood. This work reports on the temperature-dependent behavior (down to 22 K) of thermal diffusivity and conductivity of UHMWPE fibers in anticipation to observe the reduction in phonon density and scattering rate against temperature, and freeze out high momentum phonons to clearly observe the defect effects. By studying the temperature-dependent behavior of thermal reffusivity (Θ: inverse of thermal diffusivity) of UHMWPE fibers, we are able to quantify the defect effects on thermal conductivity. After taking out the amorphous region's effect, the residual thermal reffusivity (Θ0) for the studied two samples at the 0 K limit is determined as 3.45×10(4) s/m(2) and 2.95×10(4) s/m(2), respectively. For rare/none-defects crystalline materials, Θ0 should be close to zero at the 0 K limit. The defect-induced low-momentum phonon mean free path is determined as 8.06 and 9.42 nm for the two samples. They are smaller than the crystallite size in the (002) direction (19.7 nm) determined by x-ray diffraction. This strongly demonstrates the diffuse phonon scattering at the grain boundaries. The grain boundary thermal conductance (G) can be evaluated as G≈βρcpv with sound accuracy. At room temperature, G is around 3.73 GW/m(2)·K for S2, comparable to that of interfaces with tight atomic bonding.

Novel Polyethylene Fibers of Very High Thermal Conductivity Enabled by Amorphous Restructuring.

Origin of high thermal conductivity in disentangled ultra-high molecular weight polyethylene films: ballistic phonons within enlarged crystals

Constructing highly oriented and condensed shish-kebab crystalline structure of HDPE/UHMWPE blends via intense stretching process:Achieving high mechanical properties and in-plane thermal conductivity

Formation of highly oriented crystalline structure for polyoxymethylene fiber enables superior intrinsic thermal conductivity

THERMAL CONDUCTIVITY ENHANCEMENT OF POLYMERS VIA STRUCTURE TAILORING

Nanostructured Polymer Films with Metal-like Thermal Conductivity

High Thermal Conductivity of Polyethylene Nanowire Arrays Fabricated by an Improved Nanoporous Template Wetting Technique

Effect of Chain Configuration on Thermal Conductivity of Polyethylene——A Molecular Dynamic Simulation Study

Thermal Conductivity of Individual Electrospun Polymer Nanofibers

Thermal Conductivity of Electrospinning Chain-Aligned Polyethylene Oxide (PEO)

Further improvement of lattice thermal conductivity from bulk crystalline to 1-D-chain polyethylene: A high-yet-finite thermal conductivity using first-principles calculation

Thermal Conductivity of Ultra-high Molecular Weight Polyethylene Crystal: Defect-effect Uncovered by 0 K limit Phonon Diffusion.

High Thermal Conductivity Polymer Chains with Reactive Groups: a Step Towards True Application

Tropocollagen Inspired Hierarchical Spiral Structure of Organic Fibers in Epoxy Bulk for Three‐dimensional High Thermal Conductivity

Polymer Nanofibers with Outstanding Thermal Conductivity and Thermal Stability: Fundamental Linkage between Molecular Characteristics and Macroscopic Thermal Properties

High Thermal Conductive Liquid Crystal Elastomer Nanofibers

Enhancing thermal conductivity of bulk polyethylene along two directions by paved crosswise laminate

Excellent thermal conductive epoxy composites via adding UHMWPE fiber obtained by hot drawing method

Dissolving of Ultra-high Molecular Weight Polyethylene Assisted Through Supercritical Carbon Dioxide to Enhance the Mechanical Properties of Fibers

Structural evolution of ultra-high molecular weight polyethylene gel film stretching at different temperatures with reservation of shish crystals

Reversed thermal stability between stress-induced melting and recrystallized crystallites and original inclined ones in moderately stretched ultra high molecular weight polyethylene and high density polyethylene