Structure Evolution of Polyethylene-Plasticizer Film at Industrially Relevant Conditions Studied by In-Situ X-ray Scattering: the Role of Crystal Stress
Xiaowei Chen,Fei Lv,Yuanfei Lin,Zhen Wang,Lingpu Meng,Qianlei Zhang,Wenwen Zhang,Liangbin Li
DOI: https://doi.org/10.1016/j.eurpolymj.2018.02.001
IF: 6
2018-01-01
European Polymer Journal
Abstract:Structure evolution of slightly oriented high density polyethylene (HDPE)-plasticizer film is recorded with small and wide- angle X-ray scattering (SAXS/WAXS) during stretching. The HDPE has number average molecular weight (M-n) of 300 kg/mol and polydispersity index (M-w/M-n) of 20, respectively. The plasticizer is mixture of aliphatic hydrocarbon with chain length of 11-13 carbon atoms. Experiments are carried out at industrially relevant conditions, with film thickness of 650 mu m, plasticizer content of 56%, strain rate of 0.5 s(-1) and stretch temperature from 80 degrees C to 100 degrees C, respectively. An interesting evolution of SAXS patterns from anisotropic ring, four-point, six-point, and two-lobule is observed. From WAXS data, a monotonous increasing after the first decline of crystallinity is obtained, by which melting-recrystallization is validated to occur during stretching. With peak shift of WAXS pattern at different azimuthal angle (Phi), triaxial local stresses exerted on lamellae oriented along different directions are acquired. As consequence, stress exerted along and that perpendicular to chain direction are revealed to induce melting of lamellae at azimuthal angle from 0 degrees to 60 degrees and that from 60 degrees to 90 degrees, respectively. Due to the heterogeneous stress distribution of the system, the appearance of four-point SAXS pattern stems from the sequential melting of lamellae at different azimuthal angles. Through thermodynamic analysis, the physical essence of stress induced melting of lamellae is validated to be elastic energy driven crystal to amorphous phase transition.