Abstract:<p>High borated steel sheets containing 0.25 wt% to 4.0 wt% boron including hypoeutectic (0.28 wt% B and 2.11 wt% B), eutectic (2.43 wt% B) and hypereutectic (4.01 wt% B) compositions were tried to be fabricated by a novel strip casting technology, and the effects of boron content on sub-rapid solidification behavior and subsequent microstructural evolution together with mechanical properties was studied. It was found that the morphology of borides depended greatly on the boron content. When increasing boron, the morphological change of borides was network-like → grainy → cluster-like → plate-like. Various orientation relationships between different morphological borides and γ-Fe in as-cast steels were also identified. After subsequent hot-rolling and solution-treating, ultra-fine (<10 μm) borides were obtained in hypoeutectic and eutectic steels. Benefiting from that, excellent mechanical properties was achieved, which was much better than that of steels prepared by traditional ingot casting. Particularly, when the boron content approached eutectic composition, of which the effect on the microstructure and mechanical properties was more sensitive. The steels containing 2.11 wt% and 2.43 wt% boron exhibited different morphological borides with a total elongation of 14.1% and 8.0%, respectively. Moreover, a thin hypereutectic borated steel sheet was also prepared, but the borides were very large and the total elongation was very low. The correlation between microstructure and strength was clarified based on the Hall-Petch behavior and intermetallic strengthening effect. Smaller γ-grains and higher volume fraction of borides were responsible for higher strength. The plastic behavior of steels was influenced by strain-hardening rate that was determined by the volume fraction of γ-Fe matrix. A better sustainable strain-hardening capability was beneficial to extend the stage of uniform deformation and enhance the ductility. In addition, the mechanical properties of steels were also decided by the fracture mechanism that was dominated by the size of borides.</p>

Density, Surface Tension, and Viscosity of Liquid Low‐Sulfur Manganese–Boron Steel via Maximum Bubble Pressure and Oscillating Crucible Methods

Hot Ductility Behavior of Boron Containing Microalloyed Steels with Varying Manganese Contents

Densities, Surface Tensions, and Viscosities of Molten High‐Silicon Electrical Steels with Different Silicon Contents

Surface tension and density data for Fe–Cr–Mo, Fe–Cr–Ni, and Fe–Cr–Mn–Ni steels

Effect of Boron on the Solidification Characteristics and Constitutive Equation of S31254 Superaustenitic Stainless Steel

Factors Affecting Boron Yield Rate for High-Strength Steel Production

Investigation of Sulfur Influence on the Atomization of Stainless Steels

Effect of Boron on the Formation of the Naturally Deposited Film and Its Corresponding Interfacial Heat Transfer Behavior in Strip Casting of Boron-Containing Steel

DTA study and thermodynamic prediction of the solidification interval of boron 500HB abrasion-resistant steel

Effect of Boron Concentration on the Corrosion Resistance of Cast B‐bearing Steel in Molten Zinc

Liquid Phase Sintering of Boron-Containing Powder Metallurgy Steel with Chromium and Carbon

Effects of boron content on the microstructure and mechanical properties of twin-roll strip casting borated steel sheets

Effect of Boronising on Mechanical Properties, Wear and Corrosion of N80 Steel

Mechanical Properties and Fracture Mechanism of Boron-Containing 304L Austenitic Stainless Steel Densified by Liquid Phase Sintering

Liquid Phase Sintering Mechanism and Densification Behavior of Boron-Alloyed Fe-Ni-Mo-C-B Powder Metallurgy Steel

Differential Microstructure and Properties of Boron Steel Plates Obtained by Water Impinging Jet Quenching Technique

Effect of boron concentration on microstructures and properties of Fe–B–C alloy steel

Unveiling the effect of MnO/SiO2 ratios on the viscosity and structure of mold fluxes for high-Mn cryogenic steels

Stress Response Behavior, Microstructure Evolution and Constitutive Modeling of 22MnB5 Boron Steel under Isothermal Tensile Load

Effect of Silicon–Manganese Deoxidation on Oxygen Content and Inclusions in Molten Steel

Effect of Boron on Hot Ductility and Room-Temperature Tensile Properties of Microalloyed Steels with Titanium and Niobium