Abstract:<p>High borated steel sheets containing 0.25 wt% to 4.0 wt% boron including hypoeutectic (0.28 wt% B and 2.11 wt% B), eutectic (2.43 wt% B) and hypereutectic (4.01 wt% B) compositions were tried to be fabricated by a novel strip casting technology, and the effects of boron content on sub-rapid solidification behavior and subsequent microstructural evolution together with mechanical properties was studied. It was found that the morphology of borides depended greatly on the boron content. When increasing boron, the morphological change of borides was network-like → grainy → cluster-like → plate-like. Various orientation relationships between different morphological borides and γ-Fe in as-cast steels were also identified. After subsequent hot-rolling and solution-treating, ultra-fine (<10 μm) borides were obtained in hypoeutectic and eutectic steels. Benefiting from that, excellent mechanical properties was achieved, which was much better than that of steels prepared by traditional ingot casting. Particularly, when the boron content approached eutectic composition, of which the effect on the microstructure and mechanical properties was more sensitive. The steels containing 2.11 wt% and 2.43 wt% boron exhibited different morphological borides with a total elongation of 14.1% and 8.0%, respectively. Moreover, a thin hypereutectic borated steel sheet was also prepared, but the borides were very large and the total elongation was very low. The correlation between microstructure and strength was clarified based on the Hall-Petch behavior and intermetallic strengthening effect. Smaller γ-grains and higher volume fraction of borides were responsible for higher strength. The plastic behavior of steels was influenced by strain-hardening rate that was determined by the volume fraction of γ-Fe matrix. A better sustainable strain-hardening capability was beneficial to extend the stage of uniform deformation and enhance the ductility. In addition, the mechanical properties of steels were also decided by the fracture mechanism that was dominated by the size of borides.</p>

Factors Affecting Boron Yield Rate for High-Strength Steel Production

Effect of Boron Concentration on the Corrosion Resistance of Cast B‐bearing Steel in Molten Zinc

Effect of Boron on the Formation of the Naturally Deposited Film and Its Corresponding Interfacial Heat Transfer Behavior in Strip Casting of Boron-Containing Steel

Effects of boron content on the microstructure and mechanical properties of twin-roll strip casting borated steel sheets

Effect of Boron on the Solidification Characteristics and Constitutive Equation of S31254 Superaustenitic Stainless Steel

Effect of Boronising on Mechanical Properties, Wear and Corrosion of N80 Steel

The effect of boron on the properties and structure of austenitic stainless steels

Effect of Boron on Removal of Iron from Aluminium Melts

Effect of trace boron on corrosion resistance of rust layer of high-strength low-alloy steel in 3.5 wt.% NaCl solution

Effect of Boron on Delayed Fracture Resistance of Medium-Carbon High Strength Spring Steel

Influence of Boron Concentration on the Corrosion Resistance of High Boron White Cast Iron to Liquid Zinc Bath

Erosion Behavior and Mechanism of Boronised Steels

Density, Surface Tension, and Viscosity of Liquid Low‐Sulfur Manganese–Boron Steel via Maximum Bubble Pressure and Oscillating Crucible Methods

Effect of Boron Content in LiOH Solutions on the Corrosion Behavior of Zr-Sn-Nb Alloy

Effect of Heat Treatment on Structure and Wear Resistance of High Chromium Cast Steel Containing Boron

Effect of Boron on Continuous Cooling Transformation Behavior of 460B Steel

Effects of Boron Concentration on the Corrosion Resistance of Fe–B Alloys Immersed in 460°C Molten Zinc Bath

Effect of Boron on Bainitic Transformation Kinetics after Ausforming in Low Carbon Steels

Microstructure and properties of high boron bearing steel

Effect of boron concentration on microstructures and properties of Fe–B–C alloy steel

Influence of Boron on Stress-Relief Cracking Susceptibility of T23 Steel