Abstract:Two different morphologies of martensite in dual-phase (DP) steel were obtained through two processing routes. In the first method, the steel was water quenched from a fully austenitic state, followed by intercritical annealing (IA). In the second method, the steel was water quenched, cold rolled, and then subjected to intercritical annealing (C-IA). For IA and C-IA steels, the intercritical temperatures varied from 735 C-degrees to 765 C-degrees to obtain different fractions of ferrite. To understand the effect of ferrite content, morphology, and the orientation of ferrite/austenite on martensitic transformation, a combination of scanning electron microscopy, electron backscattered diffraction, and dilatometric tests were conducted. It was observed that layered martensite presented in IA samples, and blocky martensite appeared only at prior austenite boundaries at 765 C-degrees. In C-IA samples, equiaxed martensite grains were present, which become coarser by elevating the temperature to 765 C-degrees. In IA samples, martensitic transformation was much faster than in C-IA samples; the difference in martensitic transformation rate is particularly significant at lower annealing temperatures. Carbon enrichment of the partial austenite had a converse effect on the martensitic transformation at 745 C-degrees in both samples. The highest transformation rate was recorded in IA samples at 745 C-degrees among all IA and C-IA samples. The ferrite/martensite in IA samples maintained Kurdjumov-Sachs orientation relationship (K-S OR) with prior austenite and selected the same variant in the same block. Whereas, in polygonal samples, ferrite/martensite had an irrational OR with the prior austenite, no variant selection appeared in ferrite and martensite grains. Martensite nucleation accelerated on the ferrite surface when it had a K-S OR with the matrix grain, forming a low-energy interface with the ferrite. In contrast, ferrite surfaces irrationally oriented with the matrix grain did not promote martensite nucleation. This was likely due to the large misorientation and higher carbon build-up near the boundary during intercritical holding. The lower activation energy for martensitic nucleation in IA samples compared to C-IA samples resulted in an accelerated rate of martensite transformation in IA samples.

Effect of Intercritical Austenitization and Starting Matrix on Martensite Start Temperature and Austenite Carbon Concentration in Ductile Iron

Effect of austenitizing temperature and cooling rate on Ms temperature of Fe–Ni–Cr cast iron

Austenite Formation and Cementite Dissolution During Intercritical Annealing of a Medium-Manganese Steel from a Martensitic Condition

Effects of Retained Austenite upon Softening during Low-temperature Tempering in Martensitic Carbon Steels

The Influence Of Cast Structure On The Austempering Of Ductile Iron. Part 3. The Role Of Nodule Count On The Kinetics, Microstructure And Mechanical Properties Of Austempered Mn Alloyed Ductile Iron

Effect of prior austenite carbon partitioning on martensite hardening variation in a low alloy ferrite–martensite dual phase steel

The Influence of Intercritical Temperature, Ferrite-Austenite Morphology, and Orientation Relationship on Martensitic Transformation in Dual Phase Steels

Austenitizing Temperature and Cooling Rate Effects on the Martensitic Transformation in a Microalloyed-Steel

Effect of Retained Austenite on Austenite Memory of a 13% Cr–5% Ni Martensitic Steel

Effect of Prior Austenite Grain Size on Austenite Reversion, Bainite Transformation and Mechanical Properties of Fe-2Mn-0.2C Steel

Effect of Initial Microstructure on Mechanical Properties of Pressure Vessel Steel after Intercritical Heat Treatment

Influence of Carbon on the Microstructure Evolution and Hardness of Fe-13Cr-xC (x = 0-0.7 wt.%) Stainless Steel

Achieving Higher Strength and Ductility in Heavy-Section Ductile Iron Castings

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

Improvement of Critical Intergranular Fracture Stress by Increasing Carbon Content in Tempered Martensite Steels

Effect of Intercritical Temperature on the Microstructure and Mechanical Properties of a Ferritic–Martensitic Dual-Phase Low-Alloy Steel with Varying Nickel Content

Tempering Effects on the Stability of Retained Austenite and Mechanical Properties in a Medium Manganese Steel

Excess Carbon Enrichment in Austenite During Intercritical Annealing

Effect of Austempering Processes on the Tensile Properties and the Work-Hardening Behavior of Austempered Bainitic Steels Below the Martensite Start Temperature

Early Martensitic Transformation in a 0.74C–1.15Mn–1.08Cr High Carbon Steel

Effect of Austenitization Conditions on the Transformation Behavior of Low Carbon Steel Containing Ti⁻Ca Oxide Particles