Abstract:Salt crystallization represents a major reason for the damage observed for porous building materials in humid coastal areas. Despite the several theories developed to explain the process, no unanimous opinion has been proposed for the mechanism underlying the damage. A better understanding of the migration, crystallization, and distribution of salts in porous building materials in the presence of water is thus warranted to improve the durability for cultural heritages and new buildings. This paper reports an experimental study of crystal distribution, micromorphology, chloride ion migration, pore structures, and capillary absorption behaviors of cement-mortar specimens (side-coated and side-uncoated) at three different water-cement ratios (0.4, 0.6, and 0.8) after 120-day partial immersion in 5 wt% NaCl solution. Results showed that the different pore characteristics and side-coating treatment of the specimens governed not only capillary absorption, but also salt migration and distribution. The specimens with a large average pore diameter and greater porosity yielded more external salt crystals, while those with a small average pore diameter and dense surfaces demonstrated the reverse. For vertical migration, the Cl− concentration changed slightly with height of the specimens, except for the top segment. For horizontal migration, the Cl− concentrations in the central samples were higher than the edge samples. Of note, the side-coated specimens were associated with reduced external salt crystals and lower Cl− concentration in their edge samples. Compared with the salt-free specimens, both the capillary absorption coefficient (Acap) and capillary moisture content (Wcap) of the salt-contaminated specimens were lower (water-cement ratio = 0.6, −45.72%, −56.39%; water-cement ratio =0.8, −60.8%, −56.34%), illustrating the inhibitory effect of salt crystallization on the hygroscopic properties of the porous materials. Lastly, both the Acap and Wcap of the side-coated specimens were lower than uncoated ones.

Degradation Progress and Protection of Cement Mortars Partially Immersed in Sulfate–chloride Solution

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

Degradation of Mortar Fully Buried in Saline Soil Containing Sodium Sulfate or Magnesium Sulfate

Deterioration behaviors of sulfate crystallization attack on cement-based material

Chloride Ingress Profiles and Binding Capacity of Mortar in Cyclic Drying-Wetting Salt Fog Environments

Meso-Scale Mechanical Deterioration Of Mortar Subjected To Freeze Thaw Cycles And Sodium Chloride Attack

Degradation Mechanisms of Chloride Contaminated Cast-in-Situ Concrete Partially Exposed to Magnesium-Sulfate Combined Environment

Influence of Sulfate on the Chloride Diffusion Mechanism in Mortar

Degradation characteristics of Portland cement mortar incorporating supplementary cementitious materials under multi-ions attacks and drying-wetting cycles

Degradation progress of Portland cement mortar under the coupled effects of multiple corrosive ions and drying-wetting cycles

DETERIORATION CHARACTERISTICS OF CEMENT MORTAR BY PHYSICAL ATTACK OF SODIUM SULFATE

Study on the Deterioration Process of Cement‐based Materials under Sulfate Attack and Drying–wetting Cycles

Deterioration Evolutive Process of Cement-Based Materials under Sulphate Physical Crystallization Attack

Salt migration and capillary absorption characteristics of cement mortar partially immersed in NaCl solution

Effects of Cyclic Seawater Exposure on the Mechanical Performance and Chloride Penetration of Calcium Sulfoaluminate Concrete

Coupled effect of relative humidity and temperature on the degradation of cement mortars partially exposed to sulfate attack

Deterioration Mechanism of Limestone Filler Cement Mortar Exposed to Sulfate Attack at Lower Temperature

The Deterioration of Cement Mortar under the Coupled Conditions of Stray Current and Sulfate

Experiment on Cement-Based Materials with Various Compositions Against Sulfate Attack