Abstract:Some experiments were conducted to simulate the deterioration of concrete under sodium sulfate and wet-dry cycle environment in order to reveal the damage mechanism of sulfate attack.The damage development was evaluated by apparent characteristics of attacked concrete,weight changes over erosion time,profile of sulfate ions in concrete,erosion depth,degradation of compressive and splitting tensile strengths with erosion time,and deformation over attacked time.The parameters' effects such as the mass fraction of sulfate solution and the attacked time on the damage accumulation were analyzed.According to the SEM images,the damage mechanism was achieved by analyzing the microstructures of deteriorated concretes at different erosion periods.Experimental results show that the damage of concrete under sodium sulfate and wet-dry cycle environment is caused by the expansion of chemical reaction products and crystallization of sodium sulfate.The weight,strengths and ductility of concrete increase with the increase of erosion time due to the filling effect of crystals at the beginning periods.However,with the increase of erosion time,the combined expansions of ettringite,gypsum and crystal of sodium sulfate decahydrate(Na2SO4·10H2O) accelerate the evolution of damage,which results in a reduction of concrete strength and increases of weight loss and brittleness.Compared with the compressive strength,the tensile strength is more sensitive to the sulfate attacked damage due to the superimposed effect of tensile stress.

Deterioration Evolutive Process of Cement-Based Materials under Sulphate Physical Crystallization Attack

Deterioration behaviors of sulfate crystallization attack on cement-based material

Sulfate Crystallization Attack on Cement-Based Materials

DETERIORATION CHARACTERISTICS OF CEMENT MORTAR BY PHYSICAL ATTACK OF SODIUM SULFATE

Deterioration Mechanism of Plain and Blended Cement Mortars Partially Exposed to Sulfate Attack

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Study on the Deterioration Process of Cement‐based Materials under Sulfate Attack and Drying–wetting Cycles

Damage evolution of cement mortar with high volume slag exposed to sulfate attack

Degradation Progress and Protection of Cement Mortars Partially Immersed in Sulfate–chloride Solution

Deterioration Mechanisms of Sulfate Attack on Concrete under Alternate Action

Corrosion Products in Cement-Based Materials under Sulfate Partial Soaking Attack

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Development of Cementitious Materials with High Resistance to Sulfate Attack by A Combination of Emulsified Asphalt and Fly Ash

Corrosion products of cementious materials under sulfate partial soaking attack

Calculation of Expansion Stresses and Strains in Concrete under Sulfate Crystallization Attack in Dry–Wet Cycles Environments

Deterioration Mechanism of Limestone Filler Cement Mortar Exposed to Sulfate Attack at Lower Temperature

The Deterioration of Cement Mortar under the Coupled Conditions of Stray Current and Sulfate

Contradict mechanism of long-term magnesium and sodium sulfate attacks of nano silica-modified cement mortars – Experimental and thermodynamic modeling

Study on the Deterioration Characteristics of Limestone Powder Cement Mortar under Sulphate Attack at Different Temperatures

Sulfate Attack of Cement-Based Material with Limestone Filler Exposed to Different Environments