Abstract:The deterioration mechanisms of sulfate attack on concrete under sustained loading and wet-dry cycling were investigated based on micro and macroobservations. The mass fraction of sodium sulfate solution was 6.9%. Three loading levels of 20, 40, and 60% of ultimate flexural load were considered, and the load was mechanically applied to the specimens under four-point bending. Microobservations included the analysis of the chemical products formed using thermal analysis and the determination of the sulfate-ion content profile using the modified barium sulfate gravimetric method (chemical titration). Macroobservations primarily included visual observations and flexural strength changes. Test results showed that under alternate action of wet-dry cycling, concretes are attacked by expansive products such as ettringite and gypsum during the wetting cycle, and crystallization damage, induced by evaporation, is superposed during the drying cycle. Results also showed that the tensile stresses can increase diffusivity by initiating or developing microcracks; the compressive stresses are small compared with the concrete compressive strength, so any effect on ion transport properties is not obvious. Under simultaneous sulfate attack and flexural loading, deterioration is aggravated as the loading level increases, and this is characterized on the macroscale by the increased strength degradation. This research can provide some references for the assessment method of concrete structures under combined sulfate attack and loading action. DOI: 10.1061/(ASCE)MT.1943-5533.0000538. (C) 2013 American Society of Civil Engineers.

Calculation of Expansion Stresses and Strains in Concrete under Sulfate Crystallization Attack in Dry–Wet Cycles Environments

Damage Mechanism of Concrete Deteriorated by Sulfate Attack in Wet-Dry Cycle Environment

Degradation mechanism of cement mortar exposed to combined sulfate–chloride attack under cyclic wetting–drying condition

Meso-scale Mechanical Deterioration of Mortar Due to Sodium Chloride Attack

Effects of Sodium Sulfate Attack on Concrete Incorporated with Drying-Wetting Cycles

Experimental study of the deterioration mechanism of concrete under sulfate attack in wet-dry cycles

Concrete Deterioration Mechanisms under Combined Sulfate Attack and Flexural Loading

Combined effects of sulfate attack under drying–wetting cycles and loading on the fatigue behavior of concrete

Modeling of Concrete Deterioration under External Sulfate Attack and Drying-Wetting Cycles: A Review

Finite element analysis on the diffusion-reaction-damage behavior in concrete subjected to sodium sulfate attack

Damage Constitutive Model and Mechanical Performance Deterioration of Concrete under Sulfate Environment

Model of Chloride Penetration into Cracked Concrete Subject to Drying–wetting Cycles

A Chemical-Transport-Mechanics Numerical Model for Concrete under Sulfate Attack

Theoretical and Experimental Investigation of Loading Effects on Chloride Diffusion in Saturated Concrete

Estimation of Ice Formation in Mortar Saturated with Sodium Chloride Solutions

Stress Analysis for Concrete Materials under Multiple Freeze-Thaw Cycles

Influence of Flexural Loading on Chloride Ingress in Concrete Subjected to Cyclic Drying-Wetting Condition

Study on the Deterioration of Concrete under Dry-Wet Cycle and Sulfate Attack

Numerical simulation on the crystallization-induced mechanical response in hardened cement paste under external sulfate attack

A Transport-Chemical-physical–mechanical Model for Concrete Subjected to External Sulfate Attack and Drying–wetting Cycles

A multi-phase numerical simulation method for the changing process of expansion products on concrete under sulfate attack