Structural and Magnetic Properties of PrFe10Mo2Ny Prepared by Hydrogenation–disproportionation–desorption–recombination and Nitrogenation Processes
ZQ Jin,W Tang,JR Zhang,LY Lu,SL Tang,YW Du
DOI: https://doi.org/10.1016/s0304-8853(98)00127-9
IF: 3.097
1998-01-01
Journal of Magnetism and Magnetic Materials
Abstract:Hydrogenation–disproportionation–desorption–recombination (HDDR) process has been used as a pretreatment to prepare isotropic Pr(Fe,Mo)12Ny compounds. The phase component, microstructure and magnetic properties of the nitrided powders have been investigated systematically. Pr(Fe,Mo)12 absorbs interstitial hydrogen on heating at 200–350°C and forms isostructural Pr(Fe,Mo)12Hx hydrides accompanied with a slight lattice expansion corresponding to 0.9% of the cell volume. The disproportionation reaction of hydrogen with Pr(Fe,Mo)12 above 580°C results in the occurrences of PrHδ, Fe2Mo and α-Fe. As the samples hydrogenated at 750°C are degassed at 650°C in a vacuum, a metastable phase with TbCu7-type crystal structure forms. With increasing dehydrogenation temperature to 750°C, the TbCu7-type phase transforms into Pr(Fe,Mo)12 compounds. Above 850°C, Pr(Fe,Mo)12 partially decomposes and the amount of α-Fe increases. The optimum temperature for the HDDR process is 750°C for preparing the isotropic Pr(Fe,Mo)12Ny magnets. Upon nitrogenation at 425°C, the Curie temperatures of 1:7 and 1:12 type nitrides are found to be about 395 and 303°C, respectively, and a best coercivity of 3.4kOe with a magnetization up to 122emu/g at a field of 2T is obtained for 1:12 compounds without fine milling. The coercivity is probably arised by the reverse domain nucleation mechanism.